预热温度对热障涂层表面裂纹形成的影响

doi:10.7527/S1000-6893.2021.26184

论文

本期目录 | 过刊浏览 | 高级检索

前一篇 | 后一篇

预热温度对热障涂层表面裂纹形成的影响

李定骏^1,2, 杨镠育¹, 孙帆¹, 江鹏¹, 陈艺文², 王铁军¹

1. 西安交通大学航天航空学院机械结构强度与振动国家重点实验室, 西安 710049;
2. 东方电气集团东方汽轮机有限公司长寿命高温材料国家重点实验室, 德阳 618000

收稿日期:2021-08-02 修回日期:2022-06-22 出版日期:2022-06-15 发布日期:2022-07-07
通讯作者: 江鹏,E-mail:jiangpeng219@xjtu.edu.cn E-mail:jiangpeng219@xjtu.edu.cn
基金资助:
国家科技重大专项（2019-VII-0007-0147）

Effect of preheating temperature on formation of surface cracks in thermal barrier coating system

LI Dingjun^1,2, YANG Liuyu¹, SUN Fan¹, JIANG Peng¹, CHEN Yiwen², WANG Tiejun¹

1. State Key Laboratory for Strength and Vibration of Mechanical Structures, School of Aerospace Engineering, Xi'an Jiaotong University, Xi'an 710049, China;
2. State Key Laboratory of Long-Life High Temperature Materials, Dongfang Turbine Co., Ltd. of Dongfang Electric Corporation, Deyang 618000, China

Received:2021-08-02 Revised:2022-06-22 Online:2022-06-15 Published:2022-07-07
Supported by:
National Science and Technology Major Project(2019-VII-0007-0147)

摘要/Abstract

摘要： 先进航空发动机与燃气轮机热端部件的服役温度不断提高，对热障涂层性能提出了越来越高的要求。在涂层中引入一定密度的周期分布表面裂纹，可以同时提升其隔热性能和服役寿命，是一种极具潜力的先进热障涂层技术。然而，目前关于这种涂层中表面裂纹形成的力学机制研究尚不充分。以等离子喷涂热障涂层表面裂纹的形成过程为对象，发展了考虑热应力的多层结构剪切滞后模型，推导了表面裂纹形成前陶瓷层内应力场与位移场的解析解，获得了不同预热温度下陶瓷层内平均应力、平均应变能密度及总应变能随涂层厚度的演变规律，发现：在表面裂纹形成前，陶瓷层内平均应力和平均应变能密度不随其厚度改变，而总应变能随其厚度线性增大，这说明陶瓷层内总应变能是衡量能否在涂层中形成表面裂纹的关键参量；在其他喷涂参数不变的情况下，预热温度越高，表面裂纹越容易形成。本文阐明了预热温度对表面裂纹形成的影响，为实现高热障和高应变容限热障涂层的可控制备提供了理论指导。

关键词: 航空发动机, 燃气轮机, 热端部件热障涂层, 表面裂纹, 剪滞模型, 预热温度, 应变能

Abstract: Current development in advanced aero-engine and gas turbine technologies has increased the work temperature of hot components, constantly imposing higher requirements for the thermal insulation and service life of Thermal Barrier Coating system (TBCs). The introduction of periodic surface cracks with certain density into the ceramic coating to improve both thermal insulation and service life of TBCs is a new TBCs technology. However, the formation mechanism of surface cracks in the ceramic layer is still unclear. This study develops a shear-lag model considering thermal stresses in multilayer structures, and derives the analytical solutions of the stress and displacement fields in the ceramic layer before the formation of surface cracks. The evolution law of average stress, average strain energy density, and total strain energy in the plasma sprayed ceramic layer with coating thickness at different preheating temperatures is obtained. It's observed that the average stress and average strain energy density of coating layer remain the same before surface crack formation in deposition, while total strain energy keeps growing with the coating thickness, which means total strain energy is the key parameter associated with surface crack formation. Besides, it's easy to conclude that the higher preheating temperature is, the more easier surface crack formation is when the other deposition parameters are settled. The results illustrate the effect of preheating temperature on the formation of surface cracks in TBCs, providing theoretical guidance for the controllable preparation of advanced TBCs.

Key words: aero-engines, gas turbines, thermal barrier coating system for hot components, surface cracks, shear-lag model, preheating temperature, strain energy

中图分类号:

李定骏, 杨镠育, 孙帆, 江鹏, 陈艺文, 王铁军. 预热温度对热障涂层表面裂纹形成的影响[J]. 航空学报, 2022, 43(6): 526184-526184.

LI Dingjun, YANG Liuyu, SUN Fan, JIANG Peng, CHEN Yiwen, WANG Tiejun. Effect of preheating temperature on formation of surface cracks in thermal barrier coating system[J]. ACTA AERONAUTICAET ASTRONAUTICA SINICA, 2022, 43(6): 526184-526184.

参考文献

[1] 王铁军,范学领. 热障涂层强度理论与检测技术[D].西安:西安交通大学出版社,2016. WANG T J, FAN X L. Strength theory and testing technology of thermal barrier coatings[D]. Xi'an:Xi'an Jiaotong University Press, 2016(in chinese).
[2] PADTURE N P, GELL M, JORDAN E H. Thermal barrier coatings for gas-turbine engine applications[J]. Science, 2002, 296(5566):280-284.
[3] 王铁军, 范学领, 孙永乐, 等. 重型燃气轮机高温透平叶片热障涂层系统中的应力和裂纹问题研究进展[J]. 固体力学学报, 2016, 37(6):477-517. WANG T J, FAN X L, SUN Y L, et al. The stresses and cracks in thermal barrier coating system:A review[J]. Chinese Journal of Solid Mechanics, 2016, 37(6):477-517(in Chinese).
[4] CLARKE D R, OECHSNER M, PADTURE N P. Thermal-barrier coatings for more efficient gas-turbine engines[J]. MRS Bulletin, 2012, 37(10):891-898.
[5] MUKTINUTALAPATI N R. Materials for gas turbines-An overview[M]//Benini E. Advances in Gas Turbine Technology. Croatia:InTech, 2011:293-314.
[6] SAMPATH S, JIANG X Y, MATEJICEK J, et al. Substrate temperature effects on splat formation, microstructure development and properties of plasma sprayed coatings Part I:Case study for partially stabilized zirconia[J]. Materials Science and Engineering:A, 1999, 272(1):181-188.
[7] FAN X L, XU R, ZHANG W X, et al. Effect of periodic surface cracks on the interfacial fracture of thermal barrier coating system[J]. Applied Surface Science, 2012, 258(24):9816-9823.
[8] KARGER M, VAВEN R, STÖVER D. Atmospheric plasma sprayed thermal barrier coatings with high segmentation crack densities:Spraying process, microstructure and thermal cycling behavior[J]. Surface and Coatings Technology, 2011, 206(1):16-23.
[9] SAMPATH S, SCHULZ U, JARLIGO M O, et al. Processing science of advanced thermal-barrier systems[J]. MRS Bulletin, 2012, 37(10):903-910.
[10] TAYLOR T A. Thermal barrier coating for substrates and process for producing it:US5073433A[P]. 1991-12-17.
[11] GRAY D M, LAU Y C, JOHNSON C A, et al. Thermal barrier coatings having an improved columnar microstructure:US06306517B1[P]. 2001-10-23.
[12] XING Y Z, LI Y, LI C J, et al. Influence of substrate temperature on microcracks formation in plasma-sprayed yttria-stabilized zirconia splats[J]. Key Engineering Materials, 2008, 373-374:69-72.
[13] JIANG P, FAN X L, SUN Y L, et al. Bending-driven failure mechanism and modelling of double-ceramic-layer thermal barrier coating system[J]. International Journal of Solids and Structures, 2018, 130-131:11-20.
[14] MCGUIGAN A P, BRIGGS G A D, BURLAKOV V M, et al. An elastic-plastic shear lag model for fracture of layered coatings[J]. Thin Solid Films, 2003, 424(2):219-223.
[15] SHINDE S V, GILDERSLEEVE V E J, JOHNSON C A, et al. Segmentation crack formation dynamics during air plasma spraying of zirconia[J]. Acta Materialia, 2020, 183:196-206.
[16] BIAŁAS M. Finite element analysis of stress distribution in thermal barrier coatings[J]. Surface and Coatings Technology, 2008, 202(24):6002-6010.
[17] SFAR K, AKTAA J, MUNZ D. Numerical investigation of residual stress fields and crack behavior in TBC systems[J]. Materials Science and Engineering:A, 2002, 333(1-2):351-360.
[18] WIDJAJA S, LIMARGA A M, YIP T H. Modeling of residual stresses in a plasma-sprayed zirconia/alumina functionally graded-thermal barrier coating[J]. Thin Solid Films, 2003, 434(1-2):216-227.
[19] SU L C, ZHANG W X, SUN Y L, et al. Effect of TGO creep on top-coat cracking induced by cyclic displacement instability in a thermal barrier coating system[J]. Surface and Coatings Technology, 2014, 254:410-417.
[20] GUO H B, VAВEN R, STÖVER D. Atmospheric plasma sprayed thick thermal barrier coatings with high segmentation crack density[J]. Surface and Coatings Technology, 2004, 186(3):353-363.
[21] AHMANIEMI S, VUORISTO P, MÄNTYLÄ T, et al. Thermal cycling resistance of modified thick thermal barrier coatings[J]. Surface and Coatings Technology, 2005, 190(2-3):378-387.

E-mail：hkxb@buaa.edu.cn

关于我们

期刊社服务

专业学科

封面文章

友情链接

主管单位：中国科学技术协会主办单位：中国航空学会北京航空航天大学

预热温度对热障涂层表面裂纹形成的影响

Effect of preheating temperature on formation of surface cracks in thermal barrier coating system

RichHTML

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价

[1]	尹泽勇, 李概奇, 石建成, 银越千. 先进通用核心机派生发展的理念、方法及实践[J]. 航空学报, 2024, 45(7): 29713-029713.
[2]	黄维娜, 黎方娟, 祁宏斌. 航空发动机数字工程初步研究与发展思考[J]. 航空学报, 2024, 45(5): 529693-529693.
[3]	齐国宁, 吴宝海, 符江锋. 高速高压燃油齿轮泵典型卸荷槽对比分析[J]. 航空学报, 2024, 45(5): 529666-529666.
[4]	胡明辉, 高金吉, 江志农, 王维民, 邹利民, 周涛, 凡云峰, 王越, 冯家欣, 李晨阳. 航空发动机振动监测与故障诊断技术研究进展[J]. 航空学报, 2024, 45(4): 630194-630194.
[5]	陈立芳, 孙亚冰, 周书华, 高强, 乔保栋, 李栋. 基于真实数据反演的风扇转子本机平衡方法[J]. 航空学报, 2024, 45(4): 628321-628321.
[6]	马瑞贤, 王鑫, 王开明, 李斌, 廖明夫, 王四季. 航空发动机篦齿⁃橡胶涂层机匣碰摩实验[J]. 航空学报, 2024, 45(4): 628350-628350.
[7]	肖袁, 冯坤, 胡明辉, 江志农. 航空发动机转子非稳态振动分量提取方法[J]. 航空学报, 2024, 45(3): 228158-228158.
[8]	张超, 曹勇, 赵振强, 张海洋, 孙建波, 王志华, 蔚夺魁. 树脂基复合材料在民用航空发动机中的应用与关键技术研究进展[J]. 航空学报, 2024, 45(2): 28556-028556.
[9]	胡应交, 徐峰, 杨志军. 航空发动机整机防结冰试验能力综述[J]. 航空学报, 2023, 44(S2): 729449-729449.
[10]	左彦飞, 吴易柳, 王杰, 冯坤, 江志农. 温致材料属性变化对发动机双转子系统动力特性的影响[J]. 航空学报, 2023, 44(7): 226993-226993.
[11]	郑新前, 王钧莹, 黄维娜, 伏宇, 程荣辉, 熊洪洋. 航空发动机不确定性设计体系探讨[J]. 航空学报, 2023, 44(7): 27099-027099.
[12]	万能, 庄其鑫, 郭彦亨, 常智勇, 王道. 拟合精度约束下航发叶片在机测量采样策略[J]. 航空学报, 2023, 44(7): 427151-427151.
[13]	李智豪, 张彪, 李健, 许传龙, 宋兆龙. 预混旋流燃烧火焰三维折射率场重建[J]. 航空学报, 2023, 44(4): 126480-126480.
[14]	张健, 张敏, 杜娟, 黄伟亮, 聂超群. 自适应康达喷气控制在高负荷压气机中的试验研究[J]. 航空学报, 2023, 44(22): 128883-128883.
[15]	赵淼东, 胡殿印, 毛建兴, 孙海鹤, 秦仕勇, 古远兴, 王荣桥, 田腾跃, 鄢林, 肖值兴. 轮盘低周疲劳模拟件设计及试验[J]. 航空学报, 2023, 44(18): 228320-228320.