飞秒脉冲激光诱导TC4微结构表面抑冰特性实验

doi:10.7527/S1000-6893.2020.24032

Abstract

Abstract: Ice accumulation on the front edge lip of the aircraft engine intake will seriously threaten aviation safety. Bionic research shows that a hydrophobic surface with a micro-nano structure has a desirable ice suppression effect. With the aircraft lip material TC4, a TC4 microstructure surface is prepared using femtosecond pulse laser induction. A three-dimensional topography and a scanning electron microscope are used to observe the three-dimensional topography and micro-nano structure of the TC4 alloy surface. Relying on the icing characteristics experimental system to test the ice and frost resistance performance of the microstructure surface, we analyze the influence mechanism of the femtosecond pulse laser processing technology parameters on the surface microstructure and frost suppression properties. The results show that with the increase of the laser scanning speed, the depth of the arched groove formed on the surface of the TC4 alloy increases, interference fringes and circular protrusions appear above the groove, and the size of the micro-nano protrusion increases with the increase of the scanning speed. The contact angle decreases first and then increases and finally decreases; after processing, the surface droplet freezing time is delayed by 30 s compared to the unprocessed surface; at the scanning speed of 2 000 mm/s, the droplet freezing time is the longest, the frost layer quality the smallest, and the height the lowest. The micro-nano structure formed on the surface of TC4 alloy by femtosecond laser processing and the organic matter adsorbed on the surface can change the surface contact angle, and the roughness and surface morphology can affect the surface freezing time and frost amount.

Key words: femtosecond pulse laser, TC4, microstructure, wetting characteristics, frost suppression, bionic

CLC Number:

V244.1⁺5

CUI Jing, ZHANG Hang, ZHAI Wei, LU Mengke, YANG Guangfeng. Experiment on ice suppression characteristics of TC4 microstructure surface induced by femtosecond pulse laser[J]. ACTA AERONAUTICAET ASTRONAUTICA SINICA, 2021, 42(6): 424032-424032.

References

[1] YANG H, XU W, ZHAO J, et al. Predicting the probability of ice storm damages to electricity transmission facilities based on ELM and copula function[J]. Neurocomputing, 2011, 74(16):2573-2581.
[2] 杨斌. 输电线路防覆冰用超疏水自清洁涂料的制备[D]. 重庆:重庆大学, 2011:1-2. YANG B. Preparation of a super-hydrophobic and self-cleaning coating for an anti-icing transmission line[D]. Chongqing:Chongqing University, 2011:1-2(in Chinese).
[3] 毛昆朋, 潘帅锋, 陈枫, 等. 金属表面抗结冰研究进展[J]. 科技通报, 2013, 29(11):1-6. MAO K P, PAN S F, CHEN F, et al. Research progress on anti-icing modification of metals surfaces[J]. Bulletin of Science and Technology, 2013, 29(11):1-6(in Chinese).
[4] 王冠, 张德远, 陈华伟. 飞机防冰-从传统到仿生的发展[J]. 工业技术创新, 2014, 1(2):241-250 WANG G, ZHANG D Y, CHEN H W. The development of aircraft anti-icing-from traditional to bionic[J]. Industrial Technology Innovation, 2014, 1(2):241-250(in Chinese).
[5] 周家希. 大型飞机防冰系统研制发展研究[J]. 中国战略新兴产业, 2017(24):47. ZHOU J X, Research and development of large aircraft anti-icing system[J]. China Strategic Emerging Industry, 2017(24):47(in Chinese).
[6] 胡宗浩, 张明, 苏亚东. 多功能微纳表面在飞机上的应用需求与发展方向[J]. 飞机设计, 2019, 39(1):76-80. HU Z H, ZAHNG M, SU Y D. Briefly analyzing the equirement and development of multifunctional micro-nano surface on aircraft[J]. Aircraft Design, 2019, 39(1):76-80(in Chinese).
[7] 龙江游, 吴颖超, 龚鼎为, 等. 飞秒激光制备超疏水铜表面及其抗结冰性能[J]. 中国激光, 2015, 42(7):164-171. LONG J Y, WU Y C, GONG D W, et al. Femtosecond laser fabricated superhydrophobic copper surfaces and their anti-icing properties[J]. Chinese Journal of Lasers, 2015, 42(7):164-171(in Chinese).
[8] 王津, 杨辉, 王莉平, 等. 防冰疏水微结构表面的设计[J]. 航空学报, 2017, 38(S1):41-48. WANG J, YANG H, WANG L P, et al. Surface design for anti-icing and hydrophobic micro-structures[J]. Acta Aeronautica et Astronautica Sinica, 2017, 38(S1):41-48(in Chinese).
[9] 薛磊, 于竞尧, 马学胜, 等. 飞秒激光制备铜微纳结构表面的润湿及抗结冰特性研究[J]. 航空制造技术, 2018, 61(12):74-79. XUE L, YU J Y, MA X S, et al. Femtosecond laser fabricated wetting copper surfaces and their anti-icing properties[J]. Aeronautical Manufacturing Technology, 2018, 61(12):74-79(in Chinese).
[10] EBERLE P, TIWARI M K, MAITRA T, et al. Rational nanostructuring of surfaces for extraordinary icephobicity[J]. Nanoscale, 2014, 6(9):4874-4881.
[11] VERCILLO V, TONNICCHIA S, ROMANO J M, et al. Design rules for laser-treated icephobic metallic surfaces for aeronautic applications[J]. Advanced Functional Materials, 2020,30(16):1910268.
[12] YOUNG T. Experiments and calculations relative to physical optics[R]. London:Royal Society of London, 1804.
[13] WENZEL R N. Resistance of solid surfaces to wetting by water[J]. Industrial & Engineering Chemistry Research., 1936, 28(8):988-994.
[14] CASSIE A B D, BAXTER S. Wettability of porous surfaces[J]. Transactions of the Faraday Society, 1944,40:546-551.
[15] 于竞尧. 飞秒激光诱导微纳结构表面的防覆冰性能研究[D]. 长春:长春理工大学, 2018. 11-12 YU J Y. Study on anticing from micro-nano structuresurface induced by femtosecond laser[D]. Changchun:Changchun University of Science and Technology,2018. 11-12(in Chinese).
[16] DARMANIN T, GUITTARD F. Recent advances in the potential applications of bioinspired superhydrophobic materials[J]. Journal of Materials Chemistry A, 2014, 2:16319-16359.
[17] GUO P, ZHENG Y, WEN M, et al. Icephobic/anti-icing properties of micro/nanostructured surfaces[J]. Advanced Materials, 2012, 24(19):2642-2648.
[18] MEULER A J, MCKINLEY G H, COHEN R E. Exploiting topographical texture to impart icephobicity[J]. ACS Nano, 2010, 4(12):7048-7052.
[19] BOREYKO J B, SRIJANTO B R, NGUYEN T D, et al. Dynamic defrosting on nanostructured superhydrophobic surfaces[J]. Langmuir:the ACS Journal of Surfaces & Colloids, 2013, 29(30):9516-9524.
[20] KULINICH S A, FARHADI S, NOSE K, et al. Superhydrophobic surfaces:are they really ice-repellent?[J]. Langmuir the Acs Journal of Surfaces & Colloids, 2011, 27(1):25-9.
[21] CHEN J, LIU J, HE M, et al. Superhydrophobic surfaces cannot reduce ice adhesion[J]. Applied Physics Letters, 2012, 101(11):111603.
[22] MICHAEL A. HENDERSON. An HREELS and TPD study of water on TiO₂ (110):the extent of molecular versus dissociative adsorption[J]. Surface Science, 1996, 355:151-166.
[23] WANG R, SAKAI N, FUJISHIMA A, et al. Studies of surface wettability conversion on TiO₂ single-crystal surfaces[J]. Journal of Physical Chemistry B, 1999, 103(12):2188-2194.
[24] PANT R, SINGHA S, BANDYOPADHYAY A, et al. Investigation of static and dynamic wetting transitions of UV responsive tunable wetting surfaces[J]. Applied Surface Science, 2014, 292. 777-781.
[25] YANG Z, LIU X, TIAN Y. Insights into the wettability transition of nanosecond laser ablated surface under ambient air exposure[J]. Journal of Colloid and Interface Science, 2018, 533, 268-277.
[26] LIU P, CAO L, ZHAO W. Insights into the superhydrophobicity of metallic surfaces prepared by electrodeposition involving spontaneous adsorption of airborne hydrocarbons[J]. Applied Surface Science, 2015, 324, 576-583.
[27] 黄玲艳. 表面特性对冷壁面结霜过程影响的研究[D]. 北京:北京工业大学, 2011:41-64 HUANG L Y. A study on the effect of cold surface characteristics on frost formation[D]. Beijing:Beijing University of Technology, 2011:41-64(in Chinese).
[28] 许旺发. 冷面结霜机理及其抑制对策的实验研究[D]. 北京:清华大学, 2004:36-37 XU W F. Experimental studies on mechanism of formation on cold surfaces and its control[D]. Beijing:Tsinghua University, 2004:36-37(in Chinese).
[29] 王伶俐. 表面润湿性对结霜初期液滴冻结及融霜排液的影响[D]. 北京:清华大学, 2017:35 WANG L L. Effect of surface wettability on droplets freezing in the initial stage of frosting and defrosting process[D]. Beijing:Tsinghua University, 2017:35(in Chinese).

Experiment on ice suppression characteristics of TC4 microstructure surface induced by femtosecond pulse laser

RichHTML

PDF (PC)

Knowledge

Abstract

Cite this article

share this article

References

Related Articles 15

Recommended Articles

Metrics

Comments

[1]	Jiahong NIU, Haonan JIA, Fajun YI, Zujun PENG, Wei CHEN. Low-pressure thermal stability and high-temperature electrical conductivity of dense amorphous SiCN [J]. ACTA AERONAUTICAET ASTRONAUTICA SINICA, 2022, 43(S2): 152-159.
[2]	XING Yun, ZHANG Qiao, YANG Xianfeng, LIU Hua, YANG Jialing. Crashworthiness design of bio-inspired ring arrays for impact protection [J]. ACTA AERONAUTICAET ASTRONAUTICA SINICA, 2022, 43(6): 526194-526194.
[3]	WANG Miao, WANG Wei, YANG Yunlong, TAN Caiwang, WANG Gang. Effect of brazing time on microstructure and properties of SiC ceramic brazed with CoFeNiCrCu [J]. ACTA AERONAUTICAET ASTRONAUTICA SINICA, 2022, 43(4): 525057-525057.
[4]	YANG Jiankai, GU Dongdong, GE Qing, TAN Chenchen, WEN Yu. Support layout and precise forming mechanism of aluminum alloy for laser additive manufacturing [J]. ACTA AERONAUTICAET ASTRONAUTICA SINICA, 2022, 43(4): 525331-525331.
[5]	ZHANG Quanli, CHU Chenglong, ZHAI Jianchao, WANG Yukai, ZHANG Zhen, XU Jiuhua. Surface characteristics formation mechanism of ablated monocrystalline silicon by UV nanosecond pulsed laser [J]. ACTA AERONAUTICAET ASTRONAUTICA SINICA, 2022, 43(4): 525341-525341.
[6]	HU Xianliang, QIAO Hongchao, ZHAO Jibin, LU Ying, WU Jiajun, YANG Yuqi. Effect of laser shock wave on thermal corrosion resistance of single crystal alloy [J]. ACTA AERONAUTICAET ASTRONAUTICA SINICA, 2022, 43(4): 525591-525591.
[7]	ZHAO Kehan, LIU Duo, ZHU Haitao, CHEN Bin, HU Shengpeng, SONG Xiaoguo. Effect of brazing temperature on microstructure and mechanical property of C/C/AgCuTi+C_f/TC4 joint [J]. ACTA AERONAUTICAET ASTRONAUTICA SINICA, 2022, 43(4): 525007-525007.
[8]	LI Hongliang, CUI Zhanxiang, LIU Shixiong, MA Qiang, YAO Yiqiang, LEI Yucheng. Acoustic-electric characteristics and process of ultrasonic-arc MIG welding of 6061 aluminum alloy [J]. ACTA AERONAUTICAET ASTRONAUTICA SINICA, 2022, 43(2): 624969-624969.
[9]	CAI Xiaoqiang, WANG Dongpo, WANG Ying, YANG Zhenwen. Interfacial microstructure and mechanical properties of TiB₂-TiC-SiC ceramics joints fabricated by contact reactive brazing technique [J]. ACTA AERONAUTICAET ASTRONAUTICA SINICA, 2022, 43(2): 625006-625006.
[10]	LU Chuanyang, CHEN Gangqiang, TANG Xiatao, HE Yanming, YANG Jianguo, ZHENG Wenjian, MA Yinghe, LI Huaxin, GAO Zengliang. Microstructure and mechanical properties of Hastelloy N superalloy joints brazed using BNi71CrSi filler alloy [J]. ACTA AERONAUTICAET ASTRONAUTICA SINICA, 2022, 43(2): 625040-625040.
[11]	YANG Xiawei, PENG Chong, MA Tiejun, WEN Guodong, WANG Yanying, CHAI Xiaoxia, XU Yaxin, LI Wenya. Finite element analysis of fatigue crack growth of linear friction welded superalloy joints [J]. ACTA AERONAUTICAET ASTRONAUTICA SINICA, 2022, 43(2): 625004-625004.
[12]	LI Xiaopeng, HAN Rui, QIAN Xusheng, ZHANG Binggang, WANG Kehong. Effect of adding boron element on microstructure and shear strength of Ni-25at%Si/Ti600 joint [J]. ACTA AERONAUTICAET ASTRONAUTICA SINICA, 2022, 43(2): 625069-625069.
[13]	YANG Huanping, ZHUANG Wei, WANG Yaomian, YAN Wenbin. Influence of severe plastic deformation on thermal oxidation of titanium alloys [J]. ACTA AERONAUTICAET ASTRONAUTICA SINICA, 2021, 42(9): 424656-424656.
[14]	ZHANG Tiangang, ZHANG Qian, ZHUANG Huaifeng, LI Baoxuan, XU Yutong. Microstructure and properties of TiC-TiB₂ composite phase Ti-based rare earth laser cladding layers [J]. ACTA AERONAUTICAET ASTRONAUTICA SINICA, 2021, 42(7): 424139-424139.
[15]	ZHOU Tao, HE Lin, TIAN Pengfei, DU Feilong, WU Jinxing. Prediction of mechanical behavior and microstructure evolution of shear zone in orthogonal cutting 6061-T6 aluminum alloy [J]. ACTA AERONAUTICAET ASTRONAUTICA SINICA, 2021, 42(3): 423975-423975.