人工制备冰雹的力学性能试验研究

doi:10.7527/S1000-6893.2020.24255

Abstract

Abstract: The artificial hail can be used for ice collision test of various aviation accessories. Based on the ASTM F320—2010 standard, a variety of hailstones were designed and produced in this study. The mechanical properties of hailstones and the factors were investigated. A low-temperature universal testing machine was used to conduct quasi-static tests on hail. High-speed photography technology was adopted to analyze the hail crushing process and characteristics. The mechanical properties of hail under different cotton fiber types, cotton fiber characteristics, and cotton fiber content were analyzed. The results show that the cotton hail failure process can be divided into three stages: linear growth stage, yield stage, and crushing stage, with the maximum compressive strength during the failure process occurring at the end of the linear growth stage. The better the strength and elasticity of the cotton fiber, the larger the loading force required for hail breaking; the less the amount of ice attached to the cotton fiber, the smaller the loading force required for hail breaking. Increased cotton content can strengthen the connection of cotton fibers and increase the strength of cotton-containing hail; however, the hail compressive strength will not change much when the cotton content is larger than 15%. The compressive strength of hail made of hydrophilic cotton is significantly higher than that of hail containing hydrophobic cotton. The results of the study can provide reference for the verification of airworthiness compliance of civil aircraft in China.

Key words: artificial hail, high-speed photography, cotton fiber, mechanical properties, airworthiness certification

CLC Number:

V216.5⁺5

ZHANG Lifen, GE Xin, LIU Zhenxia. Experimental study on mechanical properties of artificial hail[J]. ACTA AERONAUTICAET ASTRONAUTICA SINICA, 2021, 42(2): 224255-224255.

References

[1] 胡文刚, 林长亮, 王刚, 等. 多欧拉域耦合法在平尾鸟撞中的应用[J]. 航空学报, 2020, 41(1):222860. HU W G, LIN C L, WANG G, et al. Multi-Euler domain coupling method in bird strike with flat tail[J]. Acta Aeronautica et Astronautica Sinica, 2020, 41(1):222860(in Chinese).
[2] MARCO A. A numerical model for hail impact analysis[C]//30th European Rotorcraft Forum, 2004.
[3] FIELD P R, HAND W. Hail threat standardization:EASA.2008.OP.25[R]. Cologne:European Aviation Safety Agency, 2008.
[4] ASTM. Standard test method for hail impact resistance of aerospace transparent enclosures:ASTM F320-1994[S]. West Conshohocken:ASTM International, 1994.
[5] ASTM. Standard test method for hail impact resistance of aerospace transparent enclosures:ASTM F320-2010[S]. West Conshohocken:ASTM International, 2010.
[6] 刘有丹. 民机复材结构适航设计要求和符合性方法初探[J]. 航空标准化与质量, 2012, 12(1):8-12. LIU Y D. A preliminary study on the structural airworthiness design requirements and compliance methods of civil aircraft composite materials[J]. Aviation Standardization and Quality, 2012, 12(1):8-12(in Chinese).
[7] 雷雨顺, 吴宝俊, 吴正华. 冰雹概论[M]. 北京:科学出版社, 1978:25-26. LEI Y S, WU B J, WU Z H. Introduction to hail[M]. Beijing:Science Press, 1978:25-26(in Chinese).
[8] SCHULSON E M. Brittle fracture of ice[J]. Engineering Fracture Mechanics, 2001, 68(17):1839-1887.
[9] SCHULSON E M. The structure and mechanical behavior of ice[J]. Feature Overview, 1999, 12(15):21-27.
[10] SCHULSON E M, DUVAL P. Creep and fracture of ice:Physical properties:Elasticity, friction and diffusivity[M]. Cambridge:Cambridge University Press, 2009:51-76, 101-152, 212-235.
[11] TIPPMANN J D, KIM H, RHYMER J D. Experimentally validated strain rate dependent material model for spherical ice impact simulation[J]. International Journal of Impact Engineering, 2013, 57(7):43-54.
[12] SCHULSON E M. Brittle failure of ice[J]. Engineering Fracture Mechanics, 2001, 68(17-18):1839-1887.
[13] LIST R, SCHEMENAUER R S. Free-fall behavior of planar snow crystals, conical graupel and small hail[J]. Journal of the Atmospheric Sciences, 1971, 28(1):110-115.
[14] 张永康, 李玉龙,汤忠斌, 等. 冰在低温下的单轴压缩力学行为和破坏机制[J]. 固体力学学报, 2018, 39(5):530-538. ZHANG Y K, LI Y L, TANG Z B, et al. Mechanical behavior and failure mechanism of ice at cryogenic temperatures under uniaxial compression[J]. Chinese Journal of Solid Mechanics, 2018, 39(5):530-538(in Chinese).
[15] KIM H, KEUNE J N. Compressive strength of ice at impact strain rates[J]. Journal of Materials Science, 2007, 42(8):2802-2806.
[16] CARNEY K S, BENSON D J, DUBOIS P, et al. A phenomenological high strain rate model with failure for ice[J]. International Journal of Solids & Structures, 2006, 43(25-26):7820-7839.
[17] 任晓辉. 冰的韧脆转变行为研究[D]. 大连:大连理工大学, 2005:22-34. REN X H. Investigation on ductile-to-brittle transition behavior of ice[D]. Dalian:Dalian University of Technology, 2005:22-34(in Chinese).
[18] SWIFT J M. Simulated hail ice mechanical properties and failture mechanism at quasi-static strain rates[D]. Seattle:University of Washington, 2013.
[19] 徐曼, 陈勇, 王安正. ASTM F320-2010标准冰雹的抗压力学性能实验研究[J]. 科学技术与工程, 2016, 16(16):290-294. XU M, CHEN Y, WANG A Z. Experiment on nonlinear mechanics of artificial hail based on ASTM F320-2010[J]. Science Technology and Engineering, 2016, 16(16):290-294(in Chinese).
[20] 黄兴. 含棉纤维冰的抗压性能试验[J]. 河南科技大学学报(自然科学版), 2016, 37(6):1-4. HUANG X. Experiment on compressive properties of ice with cotton fiber[J]. Journal of Henan University of Science and Technology (Natural Science), 2016, 37(6):1-4(in Chinese).
[21] 梁志会, 医用脱脂棉长度分析[J]. 标准·检验, 2012(11):64-65. LIANG Z H. An analysis of the fiber length for medical cotton[J]. Standard & Inspection, 2012(11):64-65(in Chinese).
[22] 中华人民共和国国家质量监督检验检疫总局, 中国国家标准化管理委员会. 棉花细绒棉:GB 1103-2007[S]. 北京:中国标准出版社, 2007. General Administration of Quality Supervision, Inspection and Quarantine of the People's Republic of China, Standardization Administration of the People's Republic of China. Cotton-Upland cotton:GB 1103-2007[S]. Beijing:Standards Press of China, 2007(in Chinese).
[23] 国家食品药品监督管理总局. 医用脱脂棉:YY/T 0330-2015[S]. 北京:中国标准出版社, 2016. Medicine & Medical Device of the People's Republic of China. Medical absorbent cotton:YY/T 0330-2015[S]. Beijing:Standards Press of China, 2016(in Chinese).

Experimental study on mechanical properties of artificial hail

RichHTML

PDF (PC)

Knowledge

Abstract

Cite this article

share this article

References

Related Articles 15

Recommended Articles

Metrics

Comments

[1]	Yong CHEN, Weiliang KONG, Hong LIU. Challenge of aircraft design under operational conditions of supercooled large water droplet icing [J]. ACTA AERONAUTICAET ASTRONAUTICA SINICA, 2023, 44(1): 626973-626973.
[2]	XIAO Guijian, LIU Shuai, HE Yi, LIU Gang, ZHU Shengwang, SONG Shayu. Defocus control and surface topography of titanium alloy laser belt processing [J]. ACTA AERONAUTICAET ASTRONAUTICA SINICA, 2022, 43(4): 525603-525603.
[3]	WANG Jian, YANG Xiaoyu, LI Zhuolin, WANG Haoran, WU Xiaowei, SONG Xiaoguo. Process and mechanism of low-temperature ultrasonic assisted TLP soldering of fine grain aluminum alloy [J]. ACTA AERONAUTICAET ASTRONAUTICA SINICA, 2022, 43(12): 426236-426236.
[4]	HU Shengpeng, LI Wenqiang, FU Wei, SONG Xiaoguo, LONG Weimin, CAO Jian. Interfacial microstructure and mechanical properties of high Nb containing TiAl alloy and GH3536 superalloy brazed using amorphous BNi-2 filler [J]. ACTA AERONAUTICAET ASTRONAUTICA SINICA, 2021, 42(3): 423846-423846.
[5]	WU Zhihui, NIU Gongjie, QIAN Jianping, LIU Rongzhong. Thermodynamics-based damage constitutive model and its application to damage analysis for HTPB/AP composite base bleed grain [J]. ACTA AERONAUTICAET ASTRONAUTICA SINICA, 2021, 42(3): 223855-223855.
[6]	CHEN Yueliang, ZHANG Zhuzhu, BIAN Guixue, ZHANG Yong, HUANG Hailiang. Dynamic mechanical behavior and failure model of 38CrMoAl steel under high strain rate [J]. ACTA AERONAUTICAET ASTRONAUTICA SINICA, 2020, 41(10): 423709-423709.
[7]	MA Zan, ZHOU Zhonghua, WANG Peng, HU Jianbo, KE Bingqing. Analysis of airworthiness requirements of BDS airborne equipment for aircraft tracking only [J]. ACTA AERONAUTICAET ASTRONAUTICA SINICA, 2019, 40(11): 323155-323155.
[8]	LIU Zhenguo, LIN Qiang, YA Jixuan, HU Long, WANG Yibo. Experimental research on mechanical properties of 3D full 5-direactional braided composites lugs [J]. ACTA AERONAUTICAET ASTRONAUTICA SINICA, 2016, 37(7): 2225-2233.
[9]	TIAN Wenping, XIAO Jun, LI Jinhuan, XU Ting, LIU Ting. Properties of modified cyanate resin and its composites applied to space optical structure [J]. ACTA AERONAUTICAET ASTRONAUTICA SINICA, 2016, 37(11): 3520-3527.
[10]	ZHANG Xiaochen, XIE Liyang, ZHANG Ruijin, MENG Weiying, LI Ming, HU Jiexin. ‘Coaxing effect’of prior cycling stress on material fracture mechanics performance [J]. ACTA AERONAUTICAET ASTRONAUTICA SINICA, 2016, 37(10): 3074-3082.
[11]	LI Zhiping, WANG Mengqi. Airworthiness certification method for aeroengine on stall and surge with inlet distortion [J]. ACTA AERONAUTICAET ASTRONAUTICA SINICA, 2015, 36(9): 2947-2957.
[12]	LU Zhong, RONG Xiang, ZHOU Jia, CHEN Kang. TLD analysis method of dispatch with multiple faults based on Monte Carlo simulation for FADEC system [J]. ACTA AERONAUTICAET ASTRONAUTICA SINICA, 2015, 36(12): 3970-3979.
[13]	LIU Qian, MENG Qingkun, ZHAO Xinqing, HU Liang. Evolution of Phase Constitution and Mechanical Properties of Ti-30Nb-1Mo-4Sn Alloy Subjected to Thermo-mechanical Treatment [J]. ACTA AERONAUTICAET ASTRONAUTICA SINICA, 2014, 35(10): 2826-2833.
[14]	ZHENG Ruixiao, ZHANG Yitan, MA Chaoli, MA Fengmei, XIAO Wenlong. Preparation and Investigation of Microstructure and Mechanical Properties of Ultra-high Strength Al Alloy Matrix Composites with Hybrid Nanostructure [J]. ACTA AERONAUTICAET ASTRONAUTICA SINICA, 2014, 35(10): 2802-2812.
[15]	CHEN Cihang, MING Kaisheng, BI Xiaofang. Effect of Heat Treatment on Mechanical and Magnetic Properties of FeCo-2V-0.5Cr Soft Magnetic Alloy [J]. ACTA AERONAUTICAET ASTRONAUTICA SINICA, 2014, 35(10): 2813-2818.