6061-T6铝合金激光诱导电弧焊轧复合成形组织性能

doi:10.7527/S1000-6893.2021.25880

Abstract

Abstract: Aiming at the problem that the mechanical properties of 6061-T6 heat-treat aluminum alloy are seriously decreased after welding due to "joint softening", the laser-induced arc filler wire welding and post-weld partial rolling composite forming process is proposed. The partially forced deformation of the residual height of welded joints is used to assist in strengthening the "over-aged softening zone" of the joint. The results show that the welding-rolling composite forming method can obtain well-formed and defect-free joints. Compared with welded joints, the hardness of welding-rolling composite forming joints is more uniform as a whole, and the hardness value of the most seriously softened position is increased from 71.2 HV to 87.8 HV, which is increased by 23.3%; the average tensile strength of welding-rolling composite forming joints is also increased from 246 MPa to 284 MPa, a relative increase of 15.4%, reaching up to 91.6% of the base metal. The rolling process causes partially forced deformation of the welded joint, and the dendrite crystals in the weld seam zone are compacted. The weld seam becomes wider and squeezes to both sides, and then the heat-affected zone structure is coordinating deformation, resulting in an increase in dislocation density and achieving the strengthening effect for the "over-aged softening zone".

Key words: aluminum alloy, joint softening, laser induced arc, welding-rolling composite forming, partially deformation

CLC Number:

SONG Gang, LIU Zhenfu, CHENG Jiwen, LIU Liming. Microstructure and properties of welding-rolling composite forming for 6061-T6 aluminum alloy by laser induced arc welding[J]. ACTA AERONAUTICAET ASTRONAUTICA SINICA, 2022, 43(2): 625880.

References

[1] 朱宗涛, 王雪飞, 杨晓益, 等. 高频脉冲耦合铝合金激光-MIG复合焊接熔滴过渡及其熔覆特性[J].焊接学报, 2016, 37(8):39-44, 130. ZHU Z T, WANG X F, YANG X Y, et al. Droplet transfer in aluminum alloy laser-MIG hybrid welding coupled by high frequency pulses and its cladding characteristics[J].Transactions of the China Welding Institution, 2016, 37(8):39-44, 130(in Chinese).
[2] 乔俊楠, 王启明, 邹江林, 等. 光纤激光-变极性TIG复合填丝焊接A7N01铝合金接头的组织与力学性能[J].中国激光, 2016, 43(9):0902001. QIAO J N, WANG Q M, ZOU J L, et al. Microstructure and mechanical property of A7N01 aluminum alloy joints by fiber laser-variable polarity TIG hybrid welding with filler wire[J].Chinese Journal of Lasers, 2016, 43(9):0902001(in Chinese).
[3] 翟玉峰, 黄坚, 李敏, 等. 6061-T6铝合金高速高功率CO₂激光填丝焊接性的研究[J].中国激光, 2011, 38(5):0503001. ZHAI Y F, HUANG J, LI M, et al. Research on high speed high power CO₂ laser welding of 6061-T6 aluminum with filler wire[J].Chinese Journal of Lasers, 2011, 38(5):0503001(in Chinese).
[4] 朱浩, 陈强, 陈剑虹. 热影响区几何尺寸对铝合金焊接接头变形及强度影响规律[J].焊接学报, 2012, 33(5):77-81, 117. ZHU H, CHEN Q, CHEN J H. Influence rule of HAZ geometrical dimension to aluminum alloy joint deformation and strength[J].Transactions of the China Welding Institution, 2012, 33(5):77-81, 117(in Chinese).
[5] 许良红, 田志凌, 彭云, 等. 高强铝合金的激光焊接头组织及力学性能[J].中国激光, 2008, 35(3):456-461. XU L H, TIAN Z L, PENG Y, et al. Microstructure and mechanical properties of high strength aluminum alloy laser welds[J].Chinese Journal of Lasers, 2008, 35(3):456-461(in Chinese).
[6] 王亚洁. 6061-T6铝合金高频脉冲辅助方波交流TIG焊研究[D]. 济南:山东大学, 2019:72-76. WANG Y J. Research on high-frequency pulse coupled square wave AC-TIG welding of 6061-T6 aluminum alloy[D]. Jinan:Shandong University, 2019:72-76(in Chinese).
[7] 金礼, 徐敏, 薛家祥, 等. 热输入对铝合金双脉冲MIG焊接头性能的影响[J].焊接学报, 2018, 39(1):89-92, 133. JIN L, XU M, XUE J X, et al. Effect of line energy on properties of aluminum alloy joints in double pulsed MIG welding[J].Transactions of the China Welding Institution, 2018, 39(1):89-92, 133(in Chinese).
[8] HIROSE A, KOBAYASHI K F. Characteristics of laser-beam welds of age-hardenable 6061-T6 aluminum alloy[C]//Proc SPIE 4831, First International Symposium on High-Power Laser Macroprocessing, 2003, 4831:313-318.
[9] 邱宇, 孟强, 董继红, 等. 6061-T6铝合金搅拌摩擦焊工艺及性能研究[J].塑性工程学报, 2021, 28(2):86-91. QIU Y, MENG Q, DONG J H, et al. Study on technology and properties of friction stir welding for 6061-T6 aluminum alloy[J].Journal of Plasticity Engineering, 2021, 28(2):86-91(in Chinese).
[10] 柴森森. 局部轧制及热处理对AZ系镁合金焊接组织与性能的影响研究[D]. 重庆:重庆大学, 2016:10-12. CHAI S S. Effects of partial rolling and heat treatment on the microstructure and mechanical properties of AZ series Mg alloy joints[D]. Chongqing:Chongqing University, 2016:10-12(in Chinese).
[11] 方洪渊, 董志波, 徐文立. 随焊锤击防止薄板焊接热裂纹的工艺研究[J].焊接, 2002(3):17-20. FANG H Y, DONG Z B, XU W L. Process of avoiding welding hot cracking of thin plate with trailing peening[J].Welding & Joining, 2002(3):17-20(in Chinese).
[12] 马跃进. 辊材堆焊锤击消除应力机理及随焊锤击系统研究[D]. 天津:天津大学, 2009:95-97. MA Y J. Research on stress relief mechanism by peening roll after surfacing welding and welding with trailing peening system[D]. Tianjin:Tianjin University, 2009:95-97(in Chinese).
[13] 王佳杰, 杨建国, 张敬强, 等. 随焊冲击碾压整形新方法及等承载接头拉伸与疲劳性能[J].焊接学报, 2012, 33(11):35-38, 114. WANG J J, YANG J G, ZHANG J Q, et al. A new weld shaping method with trailing impact rolling and tensile and fatigue properties for equal load-carrying capacity joints[J].Transactions of the China Welding Institution, 2012, 33(11):35-38, 114(in Chinese).
[14] 宋刚, 刘黎明, 张兆栋, 等. 一种铝合金焊接接头软化区的强韧化方法:CN111069738B[P]. 2021-11-05. SONG G, LIU L M, ZHANG Z D, et al. Strengthening and toughening method for softened area of aluminum alloy welded joint:CN111069738B[P]. 2021-11-05(in Chinese).
[15] 宋刚, 程继文, 刘振夫. 基于"热导拘束+局部变形强化"的铝合金焊轧复合成形方法[J].机械工程学报, 2020, 56(8):85-91. SONG G, CHENG J W, LIU Z F. Compound technique of welding and rolling for aluminum alloy based on thermal conductivity constraint and local deformation strengthening[J].Journal of Mechanical Engineering, 2020, 56(8):85-91(in Chinese).
[16] 刘黎明, 王红阳, 宋刚. 能源节约型激光诱导电弧复合焊技术及应用[J].焊接学报, 2015, 36(11):9-12, 113. LIU L M, WANG H Y, SONG G. Energy-saving mode laser induced arc hybrid welding technology and application[J].Transactions of the China Welding Institution, 2015, 36(11):9-12, 113(in Chinese).
[17] LIU L M, HAO X F. Study of the effect of low-power pulse laser on arc plasma and magnesium alloy target in hybrid welding by spectral diagnosis technique[J].Journal of Physics D:Applied Physics, 2008, 41(20):205202.
[18] 孙佳. 6061铝合金激光诱导TIG复合高速焊接头性能研究[D]. 大连:大连理工大学, 2019:65-67. SUN J. Study on joint property of 6061 aluminum alloy laser induced TIG hybrid weld at high welding speed[D]. Dalian:Dalian University of Technology, 2019:65-67(in Chinese).
[19] 刘强, 张南南, 张亚雄. 深冷处理对6061铝合金冷金属过渡焊接接头组织和力学性能的影响[J].热加工工艺, 2017, 46(19):244-246. LIU Q, ZHANG N N, ZHANG Y X. Effect of cryogenic treatment on microstructure and mechanical properties of 6061 aluminum alloy CMT welding joint[J].Hot Working Technology, 2017, 46(19):244-246(in Chinese).
[20] DU C C, PAN Q H, CHEN S J, et al. Effect of rolling on the microstructure and mechanical properties of 6061-T6 DS-FSW plate[J].Materials Science and Engineering:A, 2020, 772:138692.

Microstructure and properties of welding-rolling composite forming for 6061-T6 aluminum alloy by laser induced arc welding

RichHTML

PDF (PC)

Knowledge

Abstract

Cite this article

share this article

References

Related Articles 15

Recommended Articles

Metrics

Comments

[1]	Tongzhou GAO, Xiaofan HE, Xiaolei WANG, Ziguang LI, Zhentao ZHU, Zhixin ZHAN. Fatigue life prediction of 2014-T6 aluminum alloy based on CDM theory and SVM model [J]. Acta Aeronautica et Astronautica Sinica, 2024, 45(7): 228952-228952.
[2]	Yuefeng YING, Qihao CHEN, Weidong WANG, Xinyu MAO. Effect of ultrasonic vibration of welding wire on weld formation and pore in gas metal arc welding of aluminum alloy [J]. Acta Aeronautica et Astronautica Sinica, 2024, 45(2): 428711-428711.
[3]	Xiangyu WANG, Jinhui WANG, Wenhao QIU, Jintao NIU, Xiuli FU, Yang QIAO. Material removal mechanism and surface integrity of cutting titanium aluminum alloy under different cooling conditions [J]. Acta Aeronautica et Astronautica Sinica, 2024, 45(13): 629471-629471.
[4]	Lun TANG, Shengfu YU, Bo ZHENG, Yusheng SHI, Ying CHEN. Development and application of in⁃situ Al₂O₃ aluminum alloy powder core wire for cylindrical lattice [J]. ACTA AERONAUTICAET ASTRONAUTICA SINICA, 2023, 44(9): 626864-626864.
[5]	Zhongqin LIN, Zhongqi YU, Donghua DAI, Xiaoguang FAN, Shengfu YU, Dongdong GU, Shuhui LI, Yusheng SHI. Development and prospect of metal spinning: Additive hybrid manufacturing technology for complex thin⁃walled component with high ribs [J]. ACTA AERONAUTICAET ASTRONAUTICA SINICA, 2023, 44(9): 627493-627493.
[6]	Shijie JIN, Zhicheng WANG, Xin TIAN, Xu SUN, Li LIN. TOFD detection of bottom defects in aluminum alloy plate by half-skip mode wave [J]. ACTA AERONAUTICAET ASTRONAUTICA SINICA, 2023, 44(4): 426674-426674.
[7]	Pan HE, Chao LU, Wenze SHI, Ying ZHU, Guo CHEN, Liping ZHAO. Comparation of reception performance of EMATs in laser ultrasonic surface detection of aluminum alloys [J]. Acta Aeronautica et Astronautica Sinica, 2023, 44(16): 428085-428085.
[8]	Zhiqiang ZHANG, Qingze GOU, Xuecheng LU, Hao WANG, Yiran CAO, Zhiyong GUO. Droplet transfer behavior of high strength aluminum alloy CMT+P arc additive manufacturing [J]. Acta Aeronautica et Astronautica Sinica, 2023, 44(13): 427881-427881.
[9]	Tiangang ZHANG, Jiahao HUANG, Xiaoyun HOU, Zhiqiang ZHANG. Mechanism for composite paint layer on aluminum alloy surface cleaned by laser [J]. ACTA AERONAUTICAET ASTRONAUTICA SINICA, 2023, 44(11): 427656-427656.
[10]	SHI Wenze, CHENG Jinjie, HU Shuozhen, LU Chao, CHEN Yao. Application of pulse compression in electromagnetic ultrasonic guided wave detection of aluminum sheet [J]. ACTA AERONAUTICAET ASTRONAUTICA SINICA, 2022, 43(3): 425063-425063.
[11]	YANG Bingxin, MA Yunwu, SHAN He, YANG Tianhao, SUN Jing, LI Yongbing. Mechanical performance of friction self-piercing riveted joint for 2A12-T4 aluminum alloy [J]. ACTA AERONAUTICAET ASTRONAUTICA SINICA, 2022, 43(2): 625111-625111.
[12]	LI Hongliang, CUI Zhanxiang, LIU Shixiong, MA Qiang, YAO Yiqiang, LEI Yucheng. Acoustic-electric characteristics and process of ultrasonic-arc MIG welding of 6061 aluminum alloy [J]. ACTA AERONAUTICAET ASTRONAUTICA SINICA, 2022, 43(2): 624969-624969.
[13]	JIANG Chunyang, WU Lihui, CHANG Yunlong, XUE Peng, NI Dingrui, XIAO Bolv, MA Zongyi. Hybrid welding of riveting/friction stir lap joining of aluminum alloy to resin-based composite [J]. ACTA AERONAUTICAET ASTRONAUTICA SINICA, 2022, 43(2): 625190-625190.
[14]	XU Mengjia, LIU Bosheng, BI Xiaoyang, WANG Zhenmin. Effect of laser textured dual-scale structure on microstructure and mechanical property of Al/CFRPEEK joint [J]. ACTA AERONAUTICAET ASTRONAUTICA SINICA, 2022, 43(2): 624620-624620.
[15]	LIU Hao, CHEN Yuhua, ZHANG Wentao. Microstructure characteristics of Ti/Al lap joints with pinless friction stir spot welding [J]. ACTA AERONAUTICAET ASTRONAUTICA SINICA, 2022, 43(2): 624680-624680.