基体曲率对热障涂层结合强度影响的无损检测研究

Abstract

Abstract: In order to understand the failure mechanisms of the thermal barrier coatings(TBCs) applied on the aviation turbine engine blades with complex profiles, two kinds of TBC samples are prepared on plated and curvatured substrates, respectively. The evolutions of the microstructure and interface bonding strength of the TBCs during thermal cycling are investigated via AC impedance spectroscopy (IS) and Rockwell hardness (RH) indentation test. The AC IS results show that the themally grown oxide (TGO) layer thickness and micro-cracks grew with increasing thermal cycling for both samples, while an accelerated degradation is observed for the curvatured one. The RH indentation results confirm that the curvatured sample exhibites a relatively lower interface bonding strength than plated sample.

Key words: thermal barrier coatings, AC impedance spectroscopy, Rockwell hardness, curvature, bonding strength

CLC Number:

ZHAO Naiyi, PENG Hui, GUO Hongbo, GONG Shengkai. Influence of Substrate Curvature on the Bonding Strength of TBCs via Non-destructive Testing Research[J]. ACTA AERONAUTICAET ASTRONAUTICA SINICA, 2012, (6): 1125-1133.

References

[1] Jones R L. Some aspects of the hot corrosion of thermal barrier coatings. Journal of Thermal Spray Technology, 1997, 6(1): 77-84.

[2] Stringer J. Coatings in the electricity supply industry: past, present, and opportunities for the future. Surface and Coatings Technology, 1988, 108-109: 1-9.

[3] Padture N P, Gell M, Jordan E H. Thermal barrier coatings for gas-turbine engine applications. Science, 2002, 296(5566): 280-284.

[4] Wu N Q, Ogawa K, Chyu M, et al. Failure detection of thermal barrier coatings using impedance spectroscopy. Thin Solid Films, 2004, 457(2): 301-306.

[5] Ma X Q, Takemoto M. Quantitative acoustic emission analysis of plasma sprayed thermal barrier coatings subjected to thermal shock tests. Materials Science and Engineering: A, 2001, 308(1-2): 101-110.

[6] Itoh Y, Saitoh M. Evaluation of delamination crack for thermal barrier coating using infrared thermography analysis. Journal of High Temperature Society of Japan, 1995, 21: 240-247.

[7] Yi M Z, Ran L P, He J W. Advance in bonding strength test method of thick coatings. Surface Technology, 1998, 27(2): 33-37. (in Chinese) 易茂中, 冉丽萍, 何家文. 厚涂层结合强度测试方法研究进展. 表面技术, 1998, 27(2): 33-37.

[8] Zhang D B, Guo H B, Gong S K, et al. Effect of EB-PVD thermal barrier coatings on fracture characteristics of superalloy substrate. Materials Science & Technology, 2001, 9(3): 273-276.(in Chinese) 张东博, 郭洪波, 宫声凯, 等. EB-PVD热障涂层对高温合金基体断裂特征影响的研究. 材料科学与工艺, 2001, 9(3): 273-276.

[9] Anderson P S, Wang X, Xiao P. Impedance spectroscopy study of plasma sprayed and EB-PVD thermal barrier coatings. Surface and Coatings Technology, 2004, 185(1): 106-119.

[10] Wang X, Mei J F, Xiao P. Non-destructive evaluation of thermal barrier coatings using impedance spectroscopy. Journal of the European Ceramic Society, 2001, 21(7): 855-859.

[11] Song S H, Xiao P. An impedance spectroscopy study of high-temperature oxidation of thermal barrier coatings. Materials Science and Engineering: B, 2003, 97(1): 46-53.

[12] Schulz U, Schmücker M. Microstructure of ZrO₂ thermal barrier coatings applied by EB-PVD. Materials Science and Engineering: A, 2000, 276(1-2): 1-8.

[13] Li Z H, Liu C H, Liu Y C. Residual stress analysis of thermal barrier coatings with substrate curvature. Journal of North China Electric Power University, 2009, 36(4): 95-99.(in Chinese) 李志华, 刘聪慧, 刘云川. 关于基体曲率的热障涂层残余应力分析. 华北电力大学学报, 2009, 36(4): 95-99.

[14] Xu H B, Gong S K, Chen L Q, et al. Failure process of thermal barrier coatings under thermal and mechanical loading. Journal of Beijing University of Aeronautics and Astronautics, 2004, 30(10): 919-924.(in Chinese) 徐惠彬, 宫声凯, 陈立强, 等. 热、力耦合作用下热障涂层的失效机制. 北京航空航天大学学报, 2004, 30(10): 919-924.

[15] Chiang S S, Marshall D B, Evans A G. A simple method for adhesion measurements in surfaces and interfaces in ceramic-metal systems. New York: Plenum Press, 1981.

[16] Evans A G, Hutchinson J W. On the mechanics of delamination and spalling in compressed films. International Journal of Solids and Structures, 1984, 20(5): 455-466.

[17] Marshall D B, Evans A G. Measurement of adherence of residually stressed thin films by indentation I mechanics of interface delamination. Journal of Applied Physics, 1984, 56(10): 2632-2638.

Influence of Substrate Curvature on the Bonding Strength of TBCs via Non-destructive Testing Research

PDF (PC)

Knowledge

Abstract

Cite this article

share this article

References

Related Articles 15

Recommended Articles

Metrics

Comments

[1]	Yu ZENG, Hongbo WANG, Mingbo SUN, Chao WANG, Xu LIU. SST turbulence model improvements: Review [J]. ACTA AERONAUTICAET ASTRONAUTICA SINICA, 2023, 44(9): 27411-027411.
[2]	Yankuan LIU, Hang YUAN, Dinghe LI, Yujie FEI. Effect of thermal aging on mechanical properties of thermal barrier coatings interface and numerical calculation [J]. Acta Aeronautica et Astronautica Sinica, 2023, 44(20): 428507-428507.
[3]	XIA Kailong, HE Qing, ZHANG Yusheng. Measurement method of turbine blade film aperture based on infrared thermal imaging and shrinkage law [J]. ACTA AERONAUTICAET ASTRONAUTICA SINICA, 2022, 43(12): 426271-426271.
[4]	YANG Shanjie, YAN Xudong, GUO Hongbo. Failure mechanism and protection strategy of thermal barrier coatings under CMAS attack [J]. ACTA AERONAUTICAET ASTRONAUTICA SINICA, 2022, 43(10): 527613-527613.
[5]	TONG Xin, QIANG Xiaoqing, YU Peixiang, OUYANG Hua. Leading edge design method based on curvature distribution control [J]. ACTA AERONAUTICAET ASTRONAUTICA SINICA, 2021, 42(7): 124712-124712.
[6]	YANG Li, YUE Lianjie, ZHANG Xinyu. Preliminary study on wave angle and normal velocity-curvature relation of oblique detonation wave [J]. ACTA AERONAUTICAET ASTRONAUTICA SINICA, 2020, 41(11): 123701-123701.
[7]	YU Huiyong, LI Huafeng, ZENG Jie, XU Zhiwei, HUANG Jiwei, ZHAO Qidi. Monitoring technique for shape reconstruction of variable camber trailing edge based on optical fiber sensors [J]. ACTA AERONAUTICAET ASTRONAUTICA SINICA, 2020, 41(10): 223808-223808.
[8]	SONG Qinghua, LIU Weiping, LIU Xiaolin, LIU Kui, YANG Yang, CHEN Jiping. Interlaminar bonding strength for thermoplastic composite in an in-situ consolidation process [J]. ACTA AERONAUTICAET ASTRONAUTICA SINICA, 2019, 40(4): 422543-422543.
[9]	CHANG Hao, JIN Donghai, GUI Xingmin. An inlet flow model of swept blades for streamline curvature through-flow methods [J]. ACTA AERONAUTICAET ASTRONAUTICA SINICA, 2018, 39(3): 121616-121616.
[10]	LIU Yongjiao, WANG Xianfeng, XIAO Jun. Trajectory planning method for constant geodesic curvature curve of cone [J]. ACTA AERONAUTICAET ASTRONAUTICA SINICA, 2017, 38(7): 420904-420904.
[11]	QIU Ming, HAO Yan, FAN Zhaolin, JIANG Xiong, CHEN Ti. Design of single stage high efficiency fan based on arbitrary polynomial camber line airfoils [J]. ACTA AERONAUTICAET ASTRONAUTICA SINICA, 2017, 38(5): 120657-120657.
[12]	GUO Wei, DONG Lihong, WANG Huipeng, XU Binshi. Research progress of damage estimation for turbine blades based on infrared thermographic technology [J]. ACTA AERONAUTICAET ASTRONAUTICA SINICA, 2016, 37(2): 429-436.
[13]	DING Lan, MAO Xinhua, ZHU Daiyin. Polar format algorithm wavefront curvature error compensation using 2D space-variant post-filtering [J]. ACTA AERONAUTICAET ASTRONAUTICA SINICA, 2015, 36(2): 605-613.
[14]	GUO Hongbo, GONG Shengkai, XU Huibin. Research Progress on New High/ultra-high Temperature Thermal Barrier Coatings and Processing Technologies [J]. ACTA AERONAUTICAET ASTRONAUTICA SINICA, 2014, 35(10): 2722-2732.
[15]	ZHOU Jian, YANG Zhichun, HE Shun. Static Pressure Modification for Piston Theory Aerodynamics and Its Application to the Analysis of Curved Panel Flutter [J]. ACTA AERONAUTICAET ASTRONAUTICA SINICA, 2013, 34(7): 1512-1519.