缺口边疲劳小裂纹扩展特性研究

CJA 中文

导航

Academic Quality

Advertising Services |

Subscriptions |

中文

CJA

ACTA AERONAUTICAET ASTRONAUTICA SINICA ›› 1991, Vol. 12 ›› Issue (2): 115-119.

• 论文 • Previous Articles Next Articles

A STUDY ON SHORT FATIGUE CRACK GROWTH AT THE EDGE OF A NOTCH

Li Changchun¹, Zhao Huixia¹, Li Guangxia¹, Zheng Minzhong²

1. Huazhong University of Science and Technology;2. Aircraft Structure Strength Research Institute

Received:1990-06-18 Revised:1990-09-11 Online:1991-02-25 Published:1991-02-25

Abstract

Li Changchun;Zhao Huixia;Li Guangxia;Zheng Minzhong. A STUDY ON SHORT FATIGUE CRACK GROWTH AT THE EDGE OF A NOTCH[J]. ACTA AERONAUTICAET ASTRONAUTICA SINICA, 1991, 12(2): 115-119.

References

Metrics

Comments

Address: No.238, Baiyan Buiding, Beisihuan Zhonglu Road, Haidian District, Beijing, China

Postal code : 100083

E-mail：hkxb@buaa.edu.cn

Total visits: 6658907 Today visits: 1341

[1]	ZHANG Xiaochen, XIE Liyang, ZHANG Ruijin, MENG Weiying, LI Ming, HU Jiexin. ‘Coaxing effect’of prior cycling stress on material fracture mechanics performance [J]. ACTA AERONAUTICAET ASTRONAUTICA SINICA, 2016, 37(10): 3074-3082.
[2]	ZHANG Li, WU Xueren, HUANG Xinyue. Experimental investigation on the growth behavior of naturally- initiated small cracks in superalloy GH4169 [J]. ACTA AERONAUTICAET ASTRONAUTICA SINICA, 2015, 36(3): 840-847.
[3]	LIU Jianzhong;CHEN Bo;YE Xubin;HU Benrun;DING Chuanfu. Fatigue and Crack Growth Behavior of Pre-corroded Aluminum Alloy 2024-T62 and Its Life Prediction Based on Fracture Mechanics [J]. ACTA AERONAUTICAET ASTRONAUTICA SINICA, 2011, 32(1): 107-116.
[4]	TIAN Xiu-yun;SUN Zhi-qiang. Curve Fitting Study on 2024-T42 Aluminium-Alloy Fatigue Crack G rowth [J]. ACTA AERONAUTICAET ASTRONAUTICA SINICA, 2003, 24(2): 144-146.
[5]	Tao Hua . PROGRESS OF ULTRASONIC FATIGUE [J]. ACTA AERONAUTICAET ASTRONAUTICA SINICA, 1998, 19(2): 228-231.
[6]	Wang Yonglian. ESTIMATION OF FRACTURE TOUGHNESS BY FATIGUE CRACK GROWTH RATE [J]. ACTA AERONAUTICAET ASTRONAUTICA SINICA, 1997, 18(6): 728-731.
[7]	Hu Hongjiu;Li Peining;Quan Qixing;Lei Yuebao. EXPERIMENT RESEARCH OF PLASTIC STRAIN FATIGUE CRACK GROWTH IN THE NOTCH [J]. ACTA AERONAUTICAET ASTRONAUTICA SINICA, 1997, 18(3): 277-281.
[8]	Wang Zhi-zhi;Nie Xue-zhou;Wu Xiao-feng. STATISTICAL ANALYSIS OF FATIGUE CRACK GROWTH DATA [J]. ACTA AERONAUTICAET ASTRONAUTICA SINICA, 1993, 14(3): 197-201.
[9]	Liu Wen-ting;Zhao Yan-xiang. BACK-CALCULATING METHOD FOR DETERMINING PARAMETERS OF Aa/dN EQUATION OF RELATIVELY SMALL CRACK [J]. ACTA AERONAUTICAET ASTRONAUTICA SINICA, 1993, 14(2): 33-38.
[10]	Xie Ji-Zhou. LOW CYCLE FATIGUE AND FATIGUE CRACK GROWTH BEHAVIOR OF TURBINE DISK ALLOY IN718 [J]. ACTA AERONAUTICAET ASTRONAUTICA SINICA, 1993, 14(2): 79-85.
[11]	Ding Chuan-fu. INVESTIGATION OF NEAR-THRESHOLD FATIGUE CRACK PROPAGATION BEHAVIOUR IN 300M ULTRA-HIGH STRENGTH STEEL [J]. ACTA AERONAUTICAET ASTRONAUTICA SINICA, 1992, 13(8): 456-460.
[12]	Sun Jun;Li Zhong-hua;Deng Zeng-jie;Tu Ming-jing. CRACK-TIP CONSTRAINT AND J-CONTROLLING STABLE GROWTH OF CRACK IN PLANE STRESS CASE [J]. ACTA AERONAUTICAET ASTRONAUTICA SINICA, 1992, 13(5): 313-316.
[13]	Ma Jian-min;Xiao Can-Zhang;Li Nong-sheng. PREDICTING THE RESPONSE OF SHELL STRUCTURE IN THE HIGH-FREQUENCY NOISE FIELD [J]. ACTA AERONAUTICAET ASTRONAUTICA SINICA, 1992, 13(5): 317-321.
[14]	Li Zheng-neng;Li Jian-chun. STUDY ON THE SINGLE-PEAK OVERLOAD RETARDATION EFFECT OF THREE-DIMENSIONAL SMALL CRACKS [J]. ACTA AERONAUTICAET ASTRONAUTICA SINICA, 1992, 13(3): 210-213.
[15]	He Youqing;Li Zhengneng;Kou Changhe;He Qingzhi. THE MEASUREMENTS OF THE PROPAGATION AND CLOSURE OF FATIGUE SMALL CRACKS AT NOTCHES [J]. ACTA AERONAUTICAET ASTRONAUTICA SINICA, 1991, 12(2): 94-99.

A STUDY ON SHORT FATIGUE CRACK GROWTH AT THE EDGE OF A NOTCH

Knowledge

Abstract

Cite this article

share this article

References

Related Articles 15

Recommended Articles

Metrics

Comments