基于采样云纹法的CFRP正交层合板材料应变分布测量

doi:10.7527/S1000-6893.2024.30384

Abstract

Abstract:

In recent years， the development of Carbon Fiber Reinforced Polymer （CFRP） in the aviation industry has attracted much attention. Quantitative evaluation of its fracture process and damage prediction has become the key of the research. This paper established an experimental system based on the sampling Moiré method to study the evolution of interlayer strain field of a CFRP cross-ply laminate sample. The system consists of a three-point bending device， a microscope， an industrial camera and a CFRP sample with a nanoimprint grating. Using this system，a full-field measurement of the microscale strain field in the loading process of the sample， and the strain concentration level before crack occurrence was quantitatively evaluated. The results show that the initiation of interlayer cracks in CFRP is directly related to strain concentration， and obvious strain concentration occurs before crack initiation. Compared with the region around the crack， the strain concentration in the crack center is more obvious before crack initiation.With the increase of bending load， the strain concentration in the central region increases significantly， while the strain concentration in the surrounding region does not change distinctly. In the experimental method used， when the set strain of CFRP surface image is 0.1%， the root mean square error of strain measurement is less than 5×10^-5. This allows for accurate analysis of the strain field evolution of CFRP laminates before crack initiation and effectively predicts the location of crack initiation.

Key words: sampling Moiré method, carbon fiber reinforced polymer, strain field measurement, crack initiation, experimental mechanics, microscale measurement

CLC Number:

V254

Qinghua WANG, Runpeng LIU, Xiaojun YAN. Measurement of strain distribution in CFRP cross-ply laminate material based on sampling Moiré method[J]. Acta Aeronautica et Astronautica Sinica, 2024, 45(24): 430384.

Figures/Tables 13

Fig.1

Fig.2

Fig.3

Fig.4

Fig.5

Fig.6

Fig.7

Fig.8

Fig.9

Fig.10

Fig.11

Fig.12

Fig.13

References 27

[1]	赵中杰. 民用航空复合材料研究现状［C］∥ 北京粘接学会. 第八届中国国际粘接技术大会论文集. 北京：中航复合材料有限责任公司， 2023.
	ZHAO Z J. Current research status of composite materials for civil aviation［C］∥ Proceedings of the 8th China International Conference on Adhesive Technology. Beijing： AVIC Composite Corporation Ltd， 2023 （in Chinese）.
[2]	CAMANHO P P， BOWRON S， MATTHEWS F L. Failure mechanisms in bolted CFRP［J］. Journal of Reinforced Plastics and Composites， 1998， 17（3）： 205-233.
[3]	HOCHARD C， AUBOURG P A， CHARLES J P. Modelling of the mechanical behaviour of woven-fabric CFRP laminates up to failure［J］. Composites Science and Technology， 2001， 61（2）： 221-230.
[4]	SOUTIS C， TURKMEN D. Moisture and temperature effects of the compressive failure of CFRP unidirectional laminates［J］. Journal of Composite Materials， 1997， 31（8）： 832-849.
[5]	MOHAMMAD FIKRY M J， OGIHARA S. Damage behaviors in cross-ply cloth CFRP laminates cured at different temperatures［J］. Mechanical Engineering Journal， 2020， 7（5）： 20-00383.
[6]	MOHAMMAD FIKRY M J， OGIHARA S， VINOGRADOV V. Measurement of residual strains as a parameter of matrix cracking in CFRP laminates［J］. Journal of Advanced Mechanical Design， Systems， and Manufacturing， 2021， 15（4）： JAMDSM0040.
[7]	KHAN R M A， SAEIDIHARZAND S， EMAMI TABRIZI I， et al. A novel hybrid damage monitoring approach to understand the correlation between size effect and failure behavior of twill CFRP laminates［J］. Composite Structures， 2021， 270： 114064.
[8]	姜海林. 基于等效位移法的低速冲击载荷下复合材料层合板损伤力学模型［D］. 大连：大连理工大学， 2020.
	JIANG H L. Damage mechanics model of composite laminates under lowspeed impact loading based on equivalent displacement method［D］. Dalian： Dalian University of Technology， 2020 （in Chinese）.
[9]	WYSMULSKI P. Failure mechanism of tensile CFRP composite plates with variable hole diameter［J］. Materials， 2023， 16（13）： 4714.
[10]	张伟，王彬文，樊俊铃，等. 基于多模式超声成像的CFRP冲击损伤无损表征与冲击后压缩强度预测［J］. 航空学报， 2023， 44（1）： 426635.
	ZHANG W， WANG B W， FAN J L， et al. Ultrasonic nondestructive characterization of impact damage and compression after impact for CFRP based on multi-mode imaging［J］. Acta Aeronautica et Astronautica Sinica， 2023， 44（1）： 426635 （in Chinese）.
[11]	李承庚，陈振华，陈伟兵，等. CFRP层板低能冲击损伤的非线性超声兰姆波检测技术研究［J］.失效分析与预防，2021， 16（2）： 83-88， 97.
	LI C G， CHEN Z H， CHEN W B， et al. Research on nonlinear ultrasound Lamb wave detection method for low-energy impact of CFRP laminates［J］. Failure Analysis and Prevention， 2021， 16（2）： 83-88， 97 （in Chinese）.
[12]	PATHAK A K， YOKOZEKI T， IMADA M， et al. In-situ observation of tensile failure mode in cross-ply CFRP laminates using Talbot-Lau interferometry［J］. Composite Structures， 2020， 253： 112758.
[13]	MIYANO Y， NAKADA M. Accelerated testing methodology for durability of CFRP［J］. Composites Part B： Engineering， 2020， 191： 107977.
[14]	SEIFOORI S， MIRZAEI M， AFJOLAND H. Experimental and FE analysis for accurate measurement of deflection in CFRP and GFRP laminates under bending［J］. Measurement， 2020， 153： 107445.
[15]	杨正伟，赵志彬，李胤，等. 压-压疲劳载荷下CFRP层合板表面红外辐射特征［J］. 航空学报， 2021， 42（5）： 524239.
	YANG Z W， ZHAO Z B， LI Y， et al. Infrared radiation characteristics of CFRP laminate surface under compressive fatigue load［J］. Acta Aeronautica et Astronautica Sinica， 2021， 42（5）： 524239 （in Chinese）.
[16]	WANG Q H， RI S， TSUDA H， et al. Two-dimensional Moiré phase analysis for accurate strain distribution measurement and application in crack prediction［J］. Optics Express， 2017， 25（12）： 13465-13480.
[17]	CHEN R， ZHANG C H， SHI W， et al. 3D sampling Moiré measurement for shape and deformation based on the binocular vision［J］. Optics & Laser Technology， 2023， 167： 109666.
[18]	MOHAMMAD FIKRY M J， WANG Q H， IRITA M， et al. Measurement of microscopic strain distributions of CFRP laminates with fiber discontinuities by sampling Moiré method［J］. Advanced Composite Materials， 2022， 31（3）： 273-288.
[19]	WANG Q H， RI S， TSUDA H， et al. Interlaminar shear behavior of laminated carbon fiber reinforced plastic from microscale strain distributions measured by sampling Moiré technique［J］. Materials， 2018， 11（9）： 1684.
[20]	WANG Q H， OKUMURA S， RI S， et al. Second-order Moiré method for accurate deformation measurement with a large field of view［J］. Optics Express， 2020， 28（5）： 7498-7514.
[21]	WANG Q H， OKUMURA S， RI S， et al. Stereo sampling Moiré method for three-dimensional deformation mapping with a stereomicroscope［J］. Optics Express， 2022， 30（16）： 29310-29328.
[22]	WANG Q H， RI S， TSUDA H. Micro/nano-scale strain distribution measurement from sampling Moiré fringes［J］. Journal of Visualized Experiments， 2017（123）： 55739.
[23]	WANG Q H， RI S， MOHAMMAD FIKRY M J， et al. Multiplication sampling Moiré method for full-field deformation measurement of composite materials［J］. Optics Letters， 2022， 47（1）： 70-73.
[24]	SHARPEWN. Springer handbook of experimental solid mechanics［M］. Boston： Springer Science+Business Media， 2008.
[25]	MORIMOTO Y， FUJIGAKI M. Theory and application of sampling Moiré method［M］∥ Recent Advances in Mechanics. Dordrecht： Springer， 2011： 227-248.
[26]	MORIMOTO Y， FUJIGAKI M. Accuracy of sampling Moiré method［C］∥ Proceedings of International Conference on Experimental Mechanics 2008. New York： SPIE， 2008.
[27]	WANG Q H， RI S， TSUDA H， et al. Visualization and automatic detection of defect distribution in GaN atomic structure from sampling Moiré phase［J］. Nanotechnology， 2017， 28（45）： 455704.

Measurement of strain distribution in CFRP cross-ply laminate material based on sampling Moiré method

RichHTML

PDF (PC)

Knowledge

Abstract

Cite this article

share this article

Figures/Tables 13

References 27

Related Articles 15

Recommended Articles

Metrics

Comments

[1]	Jiaxuan HAN, Fan CHEN, Xuguang YANG, Zhenyu WANG, Xiaoming YUE. Experimental study on EDM of CFRP in aerosol medium [J]. Acta Aeronautica et Astronautica Sinica, 2025, 46(4): 430886-430886.
[2]	Yubin LU, Xiaohua NIE, Zhen WU. A residual stiffness prediction approach for carbon fiber reinforced composite materials based on interpretable machine learning algorithms [J]. Acta Aeronautica et Astronautica Sinica, 2025, 46(21): 532249-532249.
[3]	Jun ZOU, Zhuyi CHEN, Xiaoyu XIA, Zhenyu FENG. Fatigue life analysis of selective laser melting Al-Mg-Sc-Zr alloy based on crack initiation and propagation [J]. Acta Aeronautica et Astronautica Sinica, 2025, 46(17): 431717-431717.
[4]	Yicheng YANG, Weihua YANG, Beixuan ZHANG, Zhiheng SONG, Zhaoguo MI. Influence of friction temperature on radial crack formation in turbine blade crown fins [J]. Acta Aeronautica et Astronautica Sinica, 2025, 46(10): 231196-231196.
[5]	GAO Zhigang, HE Yuting, MA Binlin, ZHANG Tianyu. Initial fatigue quality comparison of aluminum alloy materials for aircraft wings [J]. ACTA AERONAUTICAET ASTRONAUTICA SINICA, 2021, 42(5): 524375-524375.
[6]	WANG Lianqing, HU Ya'nan, CHE Zhigang, WU Shengchuan. Fatigue performance of laser shock processed fusion welded 7075 Al alloy [J]. ACTA AERONAUTICAET ASTRONAUTICA SINICA, 2021, 42(5): 524320-524320.
[7]	XI Wei, LI Qiang, SHEN Peiliang, HE Rui, YANG Gang, LIU Shijie. Full life engineering analysis method for multiple site damage [J]. ACTA AERONAUTICAET ASTRONAUTICA SINICA, 2021, 42(5): 524328-524328.
[8]	CUI Wenbin, CHEN Xuan, CHEN Chao, CHENG Li, DING Junliang, ZHANG Hui. Damage evolution process of CFRP in very high cycle fatigue [J]. ACTA AERONAUTICAET ASTRONAUTICA SINICA, 2020, 41(1): 223212-223212.
[9]	MU Yuanwei, LU Shan. Numerical Simulation of Fatigue-crack-initiation Life for Turbine Disk Based on Material Microcosmic Characteristics [J]. ACTA AERONAUTICAET ASTRONAUTICA SINICA, 2013, 34(2): 282-290.
[10]	GONG Ming;ZHAO Jian-hua;DONG Ben-han;WANG Xian-feng;LI Cheng-zhi. INITIATION AND PROPAGATION OF FATIGUE CRACK IN EDGE REGION OF HOLE IN A SHEET WITH CENTRAL HOLE [J]. ACTA AERONAUTICAET ASTRONAUTICA SINICA, 2002, 23(3): 202-205.
[11]	Zhang Baofa;Zhou Yuequan;Fu Xiangjiong;Gan Xuedong. INVERSE RAIN FLOW COUNTING TECHNIQUE FOR CONSTRUCTING A FLIGHT BY FLIGHT LOAD SPECTRUM [J]. ACTA AERONAUTICAET ASTRONAUTICA SINICA, 1997, 18(5): 555-558.
[12]	Zhang Baofa;Fu Xiangjiong;Zhou Yuequan. TESTING RESEARCH OF LOAD SPECTRA OF AIRCRAFT [J]. ACTA AERONAUTICAET ASTRONAUTICA SINICA, 1997, 18(2): 220-223.
[13]	Ding Chuanfu;Zhao Zhenye;Song Deyu. EFFECT OF COLDWORKED HOLES ON THE INIATION LIFE AND PROPAGATION LIFE OF FATIGUE CRACKS IN TWO ULTRA-HIGH STRENGTH STEELS [J]. ACTA AERONAUTICAET ASTRONAUTICA SINICA, 1994, 15(8): 960-967.
[14]	Lu Minxu;Zheng Xiulin. EFFECT OF ENVIRONMENT MEDIUM AND STRESS RATIO ON CF CRACK INITIATION LIFE FOR 300M STEEL [J]. ACTA AERONAUTICAET ASTRONAUTICA SINICA, 1994, 15(3): 378-382.
[15]	Li Yumin;Shen Lizhong;Shi Rongming. A STUDY ON EIFS DISTRIBUTION OF AIRCRAFT STRUCTURE DETAILS [J]. ACTA AERONAUTICAET ASTRONAUTICA SINICA, 1994, 15(3): 362-365.