关键词: 日历寿命, 任意腐蚀损伤, T-H曲线

Abstract:

This paper studies out a method for deducing the T H curve of arbitrary corrosion damage which must be used in calculating the calendar life of metal corrosion. The method is original on deducing, easy to draw up and adapted for use economically. As long as there are three standard T H curves of corrosion damage as mentioned above, the T H curve of arbitrary corrosion damage may be deduced to use in calculating the metal calendar life.

Key words: calendar life, arbitrary corrosion damage, T H curve