定向凝固镍基高温合金缺口低循环疲劳性能及寿命预测

杨晓光 ,
黄佳 ,
王井科 ,
胡晓安 ,
石多奇

展开

1. 北京航空航天大学能源与动力工程学院, 北京 100191;
2. 中国人民解放军 95899 部队, 北京 100097

杨晓光,男,博士,教授,博士生导师。主要研究方向:镍基高温合金材料疲劳蠕变性能研究。Tel:010-82339071,E-mail:yxg@buaa.edu.cn;黄佳,男,博士研究生。主要研究方向:镍基定向凝固高温合金结构特征件的蠕变行为。Tel:010-82316362,E-mail:huangjia216@126.com

收稿日期: 2012-09-03

修回日期: 2012-12-25

网络出版日期: 2013-01-09

收起

Properties and Life Prediction of Low Cycle Fatigue Behavior on Notched DS Ni-based Superalloy

YANG Xiaoguang ,
HUANG Jia ,
Wang Jingke ,
HU Xiaoan ,
SHI Duoqi

Expand

1. School of Energy and Power Engineering, Beihang University, Beijing 100191, China;
2. No.95899 Unit, The Chinese People’s Liberation Army, Beijing 100097, China

Received date: 2012-09-03

Revised date: 2012-12-25

Online published: 2013-01-09

Fold

摘要

针对定向凝固(DS)镍基高温合金DZ125开展了850℃条件下不同缺口形式和不同理论应力集中系数(K_t)下的低循环疲劳(LCF)试验研究。利用弹塑性有限元分析缺口根部的应力应变场,并将传统临界距离理论(TCD)及其K_t修正形式引入SWT参数,以此开展缺口试件LCF寿命预测研究。结果表明:高温LCF强度同缺口几何形状关联不大,但具有强的K_t相关性;无论是将尖锐缺口试件作为校准试件还是对临界距离进行平均处理,传统TCD的点方法(PM)及线方法(LM)其寿命预测大于5倍分散带,且预测能力同缺口应力集中程度相关;改进TCD的点方法和线方法可得到小于2倍的分散带,且其预测精度与缺口几何形状无关。由于SWT参数可考虑平均应力(应力比)影响,故根据光滑试件和某K_t下缺口LCF试验数据便可以采用改进TCD预测其他缺口试件在不同应力比下的疲劳寿命,其应用简单、方便。

关键词： 低循环疲劳; 临界距离理论; SWT参数; Manson-Coffin方法; 定向凝固镍基高温合金

本文引用格式

杨晓光 , 黄佳 , 王井科 , 胡晓安 , 石多奇 . 定向凝固镍基高温合金缺口低循环疲劳性能及寿命预测[J]. 航空学报, 2013 , 34(7) : 1596 -1604 . DOI: 10.7527/S1000-6893.2013.0278

Abstract

Experimental investigation is carried out in this paper on the low cycle fatigue (LCF) behavior of directionally solidified (DS) Ni-based superalloy DZ125 at 850℃ with differential notch geometries and theoretical stress concentration factors (K_t). The stress-strain field at notch roots is obtained based on the elastic-plastic finite element analysis. Life prediction of notched specimens is then performed by the introduction of conventional and K_t-modified theory of critical distance (TCD) to SWT parameters. The results show that, the resistance of LCF has little to do with the geometrical shape of notch specimens but is heavily K_t-dependent. No matter by taking sharp specimens as calibration samples or dealing with critical distances by the statistical averaging method, both point method (PM) and line method (LM) of the conventional TCD exhibit that the life prediction ability related to the stress concentration factor is larger than the five times scatter band. However, a highly improved scatter band within two times can be obtained by both point and line methods of K_t-modified TCD, and the two methods are notch-geometry independent. The SWT parameter may be used to consider the effect of mean stress (stress ratio). Therefore, accurate life prediction, based on the test data of LCF of smooth specimens and just one kind of notched specimens, can be carried out using this modified TCD for other notched specimens at different stress ratios, and its application will be simple and convenient.

Key words： low cycle fatigue; theory of critical distance; SWT parameter; Manson-Coffin method; directionally solidified nickel-based superalloy

参考文献

[1] Zhou T P, Yang X G, Hou G C, et al. Experimental analysis of low-cycle and creep fatigue for directionally solidified DZ125 with a hole. Journal of Aerospace Power, 2007, 22(9): 1526-1531. (in Chinese) 周天朋, 杨晓光, 候贵仓, 等. DZ125带小孔构件低循环/保载疲劳试验与分析. 航空动力学报, 2007, 22(9): 1526-1531.
[2] Zhou T P, Yang X G, Shi D Q, et al. Modeling of low-cycle and creep fatigue life for DZ125 smooth specimens and small hole components. Journal of Aerospace Power, 2008, 23(2): 276-280. (in Chinese) 周天朋, 杨晓光, 石多奇, 等. DZ125光滑试样与小孔构件低循环/保载疲劳寿命建模. 航空动力学报, 2008, 23(2): 276-280.
[3] Manson S S. Behavior of materials under conditions of thermal stress. Washington, D.C.: National Advisory Commission on Aeronautics, 1953.
[4] Coffin L F, Jr. A study of the effects of cyclic thermal stress on a ductile metal. New York: Knolls Atomic Power Laboratory, 1953.
[5] Morrow J. Fatigue design handbook-advances in engineering. Warrendale, PA: Society of Automotive Engineers, 1968: 21-29.
[6] Smith K N, Watson P, Topper T H. A stress-strain function for the fatigue of metals. Journal of Materials, 1970, 5(4): 767-778.
[7] Yao W, Xia K, Gu Y. On the fatigue notch factor, K_f. International Journal of Fatigue, 1995, 17(4): 245-251.
[8] Bentachfine S, Pluvinage G, Gilgert J, et al. Notch effect in low cycle fatigue. International Journal of Fatigue, 1999, 21(5): 421-430.
[9] Neuber H. Theory of notch stresses: principles for exact stress calculation. Ann Arbor, MI: JW Edwards, 1946.
[10] Peterson R E. Notch sensitivity. Sines G, Waisman J L. Metal fatigue. New York: McGraw Hill, 1959: 293-306.
[11] Taylor D. Geometrical effects in fatigue: a unifying theoretical model. International Journal of Fatigue, 1999, 21(5): 413-420.
[12] Susmel L, Taylor D. A novel formulation of the theory of critical distances to estimate lifetime of notched components in the medium-cycle fatigue regime. Fatigue and Fracture of Engineering Materials and Structures, 2007, 30(7): 567-581.
[13] Susmel L, Taylor D. On the use of the theory of critical distances to estimate fatigue strength of notched components in the medium-cycle fatigue regime. Proceedings of Fatigue, 2006, 2006.
[14] Susmel L, Atzori B, Meneghetti G, et al. Notch and mean stress effect in fatigue as phenomena of elasto-plastic inherent multiaxiality. Engineering Fracture Mechanics, 2011, 78(8): 1628-1643.
[15] GB/T 15248—1994. The test method for axial loading constant amplitude low cycle fatigue of metallic materials. Beijing: Standards Press of China, 1994: 1-17. (in Chinese) GB/T 15248—1994. 金属材料轴向等幅低循环疲劳试验方法. 北京: 中国标准出版社, 1994: 1-17.
[16] HB 5287—1996. The test method for axial loading on low cycle fatigue of metallic materials. Beijing: Standards Press of China, 1996: 1-22. (in Chinese) HB 5287—1996. 金属材料轴向加载疲劳试验方法. 北京: 中国标准出版社, 1996: 1-22.
[17] Susmel L, Taylor D. An elasto-plastic reformulation of the theory of critical distances to estimate lifetime of notched components failing in the low/medium-cycle fatigue regime. Journal of Engineering and Technology, 2010, 132(2): 210021-210028.
[18] China aeronautic material handbook (internal publication). Beijing: Institute of Aeronautical Materials, 2004:171-213. (in Chinese) 中国航空材料手册(内部使用). 北京: 北京航空材料研究院, 2004: 171-213.
[19] Yang X G, Wang J K, Liu J L. High temperature LCF life prediction of notched DS Ni-based superalloy using critical distance concept. International Journal of Fatigue, 2011, 33(11): 1470-1476.

Options

文章导航

模态框（Modal）标题

摘要

本文引用格式

Abstract

参考文献