Effect of delamination depth on compressive properties of aircraft composite laminates

Ziang LIU; Xitao ZHENG; Yingshi CHEN; Tianze DENG; Weijie MA

doi:10.7527/S1000-6893.2025.32340

ACTA AERONAUTICAET ASTRONAUTICA SINICA >

2025 , Vol. 46 >Issue 21: 532340 - 532340

DOI: https://doi.org/10.7527/S1000-6893.2025.32340

Special Issue: 60th Anniversary of Aircraft Strength Research Institute of China

Effect of delamination depth on compressive properties of aircraft composite laminates

Ziang LIU ,
Xitao ZHENG ,
Yingshi CHEN ,
Tianze DENG ,
Weijie MA

Expand

^1.School of Aeronautics，Northwestern Polytechnical University，Xi’an 710072，China
^2.National Key Laboratory of Strength and Structural Integrity，Xi’an 710072，China
^3.Aviation Key Lab of Science and Technology on High Performance Electromagnetic Windows，AVIC Research Institute for Special Structures of Aeronautical Composite，Jinan 250023，China

E-mail： zhengxt@nwpu.edu.cn

Received date: 2025-05-30

Revised date: 2025-06-17

Accepted date: 2025-08-21

Online published: 2025-09-05

Supported by

National Key Research and Development Program of China(2023YFB3709603);Aeronautical Science Foundation of China(ASFC-20230015053005)

Fold

Abstract

Aircraft composite laminates are susceptible to delamination damage throughout their lifecycle， from manufacturing to in-service operation. The existence of delamination damage results in a significant degradation in structural strength， stiffness， and stability， which can induce early instability and precipitate global failure. Therefore， it is necessary to explore the influence of delamination damage on the mechanical properties of composite laminates. Addressing the material selection for delamination-critical regions in aircraft structures is an imperative research objective. Further analysis is warranted to understand how delamination depth affects the mechanical behavior of composite structures. Therefore， four kinds of carbon fiber reinforced epoxy resin matrix composites were selected for single delamination damage and impact damage （gradient delamination damage）. Quasi-static compression， low-velocity impact and compression after impact tests were carried out to compare the compressive residual strength of four composite laminates with delamination damage. Combined with finite element simulation， the influence trend of delamination depth on the compression performance of composite laminates is explored， and the reason for this trend is analyzed. The results show that compared with the unidirectional prepreg， the selection of high strength fabric prepreg in delamination-critical regions of the aircraft structure will bring better results， and the maximum compressive residual strength can be increased by 118.31%. Additionally， different delamination depths will lead to the bearing capacity of composite laminates determined by different sub-plates. The influence of delamination damage on the compressive properties of aircraft composite laminates has been discussed in depth， which provides a research basis for the damage tolerance design of aircraft composite structures.

Key words： aircraft composite structures; laminates; delamination damage; compressive properties; delamination depth

Cite this article

Ziang LIU , Xitao ZHENG , Yingshi CHEN , Tianze DENG , Weijie MA . Effect of delamination depth on compressive properties of aircraft composite laminates[J]. ACTA AERONAUTICAET ASTRONAUTICA SINICA, 2025 , 46(21) : 532340 -532340 . DOI: 10.7527/S1000-6893.2025.32340

References

[1]	赵丽滨，龚愉，张建宇. 纤维增强复合材料层合板分层扩展行为研究进展［J］. 航空学报， 2019， 40（1）： 522509.
	ZHAO L B， GONG Y， ZHANG J Y. A survey on delamination growth behavior in fiber reinforced composite laminates［J］. Acta Aeronautica et Astronautica Sinica， 2019， 40（1）： 522509 （in Chinese）.
[2]	刘向民，姚卫星，陈方. 复合材料层合板结构冲击损伤数值模拟的损伤力学模型［J］. 航空学报， 2016， 37（10）： 3054-3063.
	LIU X M， YAO W X， CHEN F. Damage mechanics model for simulating impact responses of composite laminated structures［J］. Acta Aeronautica et Astronautica Sinica， 2016， 37（10）： 3054-3063 （in Chinese）.
[3]	张海燕，李根臣，刘震宇，等. 国产T700级碳纤维及复合材料性能表征［J］. 化工新型材料， 2020， 48（4）： 238-240.
	ZHANG H Y， LI G C， LIU Z Y， et al. Characterization of domestic T700 carbon fiber and its composites［J］. New Chemical Materials， 2020， 48（4）： 238-240 （in Chinese）.
[4]	张磊，张丽，郑洁. T800级碳纤维复合材料结构压缩设计许用值确定方法研究［J］. 纤维复合材料， 2021， 38（2）： 56-58.
	ZHANG L， ZHANG L， ZHENG J. Research on determining structural compressed design allowable of T800 composites［J］. Fiber Composites， 2021， 38（2）： 56-58 （in Chinese）.
[5]	郑晓霞，郑锡涛，沈真，等. 低速冲击与准静态压痕力下复合材料层合板的损伤等效性［J］. 航空学报， 2010， 31（5）： 928-933.
	ZHENG X X， ZHENG X T， SHEN Z， et al. Damage equivalent of composite laminates subjected to drop-weight impact and quasi-static indentation force［J］. Acta Aeronautica et Astronautica Sinica， 2010， 31（5）： 928-933 （in Chinese）.
[6]	ZHANG C， HE E M， ZHU K Y， et al. Delamination propagation manipulation of composite laminates under low-velocity impact and residual compressive strength evaluation［J］. Engineering Fracture Mechanics， 2024， 307： 110333.
[7]	ZHANG C， ZHENG X T， ZHU K Y， et al. Experimental investigation of low-velocity impact behavior and CAI on composite laminates by discrete interleaved toughening［J］. Mechanics of Advanced Materials and Structures， 2024， 31（11）： 2460-2471.
[8]	ZHU K Y， ZHENG X T， PENG J， et al. The relationship between the impact position interference and CAI strength of composite sandwich structures under double impacts［J］. Composites Part B： Engineering， 2024， 268： 111092.
[9]	孙先念，陈浩然，陈绍杰. 含分层损伤复合材料层合板前后屈曲行为研究［J］. 航空学报， 1999， 20（3）： 224-229.
	SUN X N， CHEN H R， CHEN S J. Pre postbuckling analysis of composite laminates with delamination damage［J］. Acta Aeronautica et Astronautica Sinica， 1999， 20（3）： 224-229.
[10]	王雪明，谢富原，李敏，等. 热压罐成型复合材料复杂结构对制造缺陷的影响规律［J］. 航空学报， 2009， 30（4）： 757-762.
	WANG X M， XIE F Y， LI M， et al. Effect rules of complex structure on manufacturing defects for composites in autoclave molding［J］. Acta Aeronautica et Astronautica Sinica， 2009， 30（4）： 757-762 （in Chinese）.
[11]	许洪明，温卫东，刘芳. 含分层缺陷复合材料层合板压缩强度试验研究［J］. 航空发动机， 2013， 39（3）： 73-76.
	XU H M， WEN W D， LIU F. Compressive strength experimentation research on composite laminates layered defect［J］. Aeroengine， 2013， 39（3）： 73-76 （in Chinese）.
[12]	MEI H， TAN Y F， ZHANG D， et al. A novel delamination defects designed for understanding mechanical degradation in a laminated C/SiC composites［J］. Journal of Alloys and Compounds， 2019， 770： 1138-1146.
[13]	YU M M， LIU H X， XIAO R B， et al. Residual strength and failure mechanism of CF/PPS composites with delamination damage［J］. Polymer Composites， 2024， 45（13）： 12391-12404.
[14]	CHENG P， PENG Y， WANG K， et al. Mechanical performance and damage behavior of delaminated composite laminates subject to different modes of loading［J］. Journal of the Brazilian Society of Mechanical Sciences and Engineering， 2021， 43（10）： 455.
[15]	ASLAN Z， ?AHIN M. Buckling behavior and compressive failure of composite laminates containing multiple large delaminations［J］. Composite Structures， 2009， 89（3）： 382-390.
[16]	周睿，关志东，贾云超，等. 分层缺陷对复合材料层板压缩性能的影响［J］. 北京航空航天大学学报， 2015， 41（2）： 311-317.
	ZHOU R， GUAN Z D， JIA Y C， et al. Effects of delamination on compressional properties of composite laminate［J］. Journal of Beijing University of Aeronautics and Astronautics， 2015， 41（2）： 311-317 （in Chinese）.
[17]	LI Y L， WANG B， ZHOU L. Study on the effect of delamination defects on the mechanical properties of CFRP composites［J］. Engineering Failure Analysis， 2023， 153： 107576.
[18]	BAI Y J， XU Z H， SONG J R， et al. Experimental and numerical analyses of stiffened composite panels with delamination under a compressive load［J］. Journal of Composite Materials， 2020， 54（9）： 1197-1216.
[19]	HU C X， BAI Y J， XU Z H， et al. Progressive damage behavior of composite L-stiffened structures with initial delamination defects under uniaxial compression： Experimental and numerical investigations［J］. Polymer Composites， 2022， 43（6）： 3765-3781.
[20]	LAPCZYK I， HURTADO J A. Progressive damage modeling in fiber-reinforced materials［J］. Composites Part A： Applied Science and Manufacturing， 2007， 38（11）： 2333-2341.
[21]	HASHIN Z. Fatigue failure criteria for unidirectional fiber composites［J］. Journal of Applied Mechanics， 1981， 48（4）： 846-852.
[22]	ZHOU J J， WEN P H， WANG S N. Finite element analysis of a modified progressive damage model for composite laminates under low-velocity impact［J］. Composite Structures， 2019， 225： 111113.
[23]	KHAZAIE M， ESLAMI-FARSANI R， SAEEDI A. Evaluation of repeated high velocity impact on polymer-based composites reinforced with basalt and Kevlar fibers［J］. Materials Today Communications， 2018， 17： 76-81.
[24]	沈真，杨胜春，陈普会. 复合材料抗冲击性能和结构压缩设计许用值［J］. 航空学报， 2007， 28（3）： 561-566.
	SHEN Z， YANG S C， CHEN P H. Behaviors of composite materials to withstand impact and structural compressive design allowableness［J］. Acta Aeronautica et Astronautica Sinica， 2007， 28（3）： 561-566 （in Chinese）.
[25]	沈真，陈普会，唐啸东，等. 复合材料结构设计值和冲击损伤容限许用值［J］. 航空学报， 1993， 14（12）： 575-582.
	SHEN Z， CHEN P H， TANG X D， et al. Composite structure design values and impact damage tolerance allowables［J］. Acta Aeronautica et Astronautica Sinica， 1993， 14（12）： 575-582 （in Chinese）.
[26]	沈真. 复合材料飞机结构设计许用值及其确定原则［J］. 航空学报， 1998， 19（4）： 385-392.
	SHEN Z. Design allowables of composite aircraft structures and their determination principles［J］. Acta Aeronautica et Astronautica Sinica， 1998， 19（4）： 385-392.

Options

Outlines

模态框（Modal）标题

Abstract

Cite this article

References