Effect of high density pulse current on healing of cracks of SiCp/Al composites
Received date: 2017-02-28
Revised date: 2017-07-20
Online published: 2017-07-20
Supported by
National Natural Science Foundation of China (51405487)
In order to solve the problem that SiCp/Al composites is low in plasticity and prone to crack, Specimens of SiCp/Al composites with drawing cracks are used to perform healing experiment by high density (31.25 A/mm2) pulse current treating. After pre-cracking with mechanical tensile at room temperature, the Scanning Electron Microscope (SEM) figures of the cracks taken before and after the healing are compared. The effects of pulse current treating on the mechanical properties are studied. Experimental results show that the local closure, the decrease in width and local melting around the crack tip are observed after a high density pulse current was applied to a specimen. The specific elongation of the specimen with the crack increases by 38% after healing. Based on the coupled current-thermal-structural theory, a numerical simulation method is proposed to study the electric current field, the temperature field and the stress field around the crack of the SiCp/Al sheet. Based on the results of numerical simulation, the mechanism of healing crack with pulse current is studied to provide some foundation for application of high density pulse current healing techniques.
Key words： SiCp/Al composites; crack healing; pulse current; elongation; numerical simulation
YI Zhuoxun , LAI Xiaoming , WANG Bo , ZHANG Jiabo . Effect of high density pulse current on healing of cracks of SiCp/Al composites[J]. ACTA AERONAUTICAET ASTRONAUTICA SINICA, 2017 , 38(11) : 221197 -221197 . DOI: 10.7527/S1000-6893.2017.221197
[1] LI D S, ZHOU X L, ZOU A H, et al. Fabrication and fracture analyses of SiC particulate-reinforced Al matrix composites[J]. Advanced Materials Research, 2013, 764(2533):43-46.
[2] WANG B, WANG G F, JIANG S S, et al. Effect of pulse current on thermal performance and deep drawing of SiCp/2024Al composite sheet[J]. International Journal of Advanced Manufacturing Technology, 2013, 67(1-4):623-627.
[3] 付宇明, 赵华洋, 杜文连, 等. 含孔洞缺陷焊接接头放电强化及疲劳寿命分析[J]. 焊接学报, 2017(4):31-34. FU Y M, ZHAO H Y, DU W L, et al. Fatigue life and strengthening research of welded joints with hole defects by using electromagnetic heating[J]. Transactions of the China Welding Institution, 2017(4):31-34(in Chinese).
[4] 詹志新, 佟阳, 李彬恺, 等. 考虑冲击缺陷的钛合金板的疲劳寿命预估[J]. 航空学报, 2016, 37(7):2200-2207. ZHAN Z X, TONG Y, LI B K, et al. Fatigue life prediction for titanium plate considering impact defect[J]. Acta Aeronautica et Astronautica Sinica, 2016, 37(7):2200-2207(in Chinese).
[5] 祝青钰, 韩峰, 隋明丽. 无限大板孔边双裂纹应力强度因子和裂纹面张开位移[J]. 航空学报, 2016, 37(3):883-893. ZHU Q Y, HAN F, SUI M L. Stress intensity factors and crack-surface opening displacements for two cracks emanating from a circular hole in an infinite plate[J]. Acta Aeronautica et Astronautica Sinica, 2016, 37(3):883-893(in Chinese).
[6] 于静. 基于强脉冲电流金属材料裂纹止裂及愈合技术研究[D]. 大连:大连理工大学, 2014:28-33. YU J. Technology study on crack arrest and healing by high-density pulse current[D]. Dalian:Dalian University of Technology, 2014:28-33(in Chinese).
[7] 周亦胄, 周本濂, 郭晓楠, 等. 脉冲电流对45钢损伤的恢复作用[J]. 材料研究学报, 2000, 14(1):29-36. ZHOU Y Z, ZHOU B L, GUO X N, et al. Reversing effect of electric current pulse on the damage of 45 steel[J]. Chinese Journal of Materials Research, 2000, 14(1):29-36(in Chinese).
[8] 王浩, 王立文, 王涛, 等. 航空发动机损伤叶片再制造修复方法与实现[J]. 航空学报, 2016, 37(3):1036-1048. WANG H, WANG L W, WANG T, et al. Method and implementation of remanufacture and repair of aircraft engine damaged blades[J]. Acta Aeronautica et Astronautica Sinica, 2016, 37(3):1036-1048(in Chinese).
[9] 付宇明, 白象忠, 郑丽娟, 等. 铝合金薄板中裂纹的电磁热效应局部跨越止裂[J]. 航空学报, 2002, 23(3):282-284. FU Y M, BAI X Z, ZHENG L J, et al. Crack arrest in aluminum alloy plate by part crossover using electromagnetic heat effects[J]. Acta Aeronautica et Astronautica Sinica, 2002, 23(3):282-284(in Chinese).
[10] 付宇明, 王宁宁, 郭建龙, 等. 含半圆形埋藏裂纹金属构件脉冲放电时应力场分析[J]. 中国机械工程, 2015, 26(4):536-540. FU Y M, WANG N N, GUO J L, et al. Analysis of stress field at time of pulse discharge in metal structure with semicircle embedding crack[J]. China Mechanical Engineering, 2015, 26(4):536-540(in Chinese).
[11] 田振国, 郑坚, 白象忠, 等. 含环向裂纹厚壁圆筒电磁止裂的应力场分析[J]. 航空学报, 2005, 26(6):701-705. TIAN Z G, ZHENG J, BAI X Z, et al. Analysis of stress field in thick cylinder with circular crack arrested by electromagnetic heating[J]. Acta Aeronautica et Astronautica Sinica, 2005, 26(6):701-705(in Chinese).
[12] ZHENG L J, FU Y M. Analysis on the temperature field when crack arresting in an axial symmetry metal die by pulse current discharged[J]. Key Engineering Materials, 2007, 348-349:765-768.
[13] 付宇明, 郭建龙, 郑丽娟. 带有疲劳裂纹的35CrMo构件电磁热止裂强化[J]. 机械工程学报, 2015, 51(4):66-70. FU Y M, GUO J L, ZHENG L J. Crack arrest of 35CrMo component with fatigue crack by electromagnetic heating[J]. Journal of Mechanical Engineering, 2015, 51(4):66-70(in Chinese).
[14] 付宇明, 吴杰, 康玮明, 等. 2A12铝合金试件中空间斜裂纹在线止裂及性能分析[J]. 航空学报, 2008, 29(4):1073-1078. FU Y M, WU J, KANG W M, et al. On-line crack prevention and performance analysis of aluminum alloy 2A12 specimen with oblique crack[J]. Acta Aeronautica et Astronautica Sinica, 2008, 29(4):1073-1078(in Chinese).
[15] 付宇明, 王俊丽, 郑丽娟, 等. 含有裂纹的Al-Mg合金构件电磁热止裂[J]. 中国有色金属学报, 2013, 23(1):29-34. FU Y M, WANG J L, ZHENG L J, et al. Crack arrest of Al-Mg alloy component with cracks by electromagnetic heating[J]. The Chinese Journal of Nonferrous Metals, 2013, 23(1):29-34(in Chinese).
[16] 张洪潮, 于静, 郝胜智, 等. 电磁场的热效应在再制造毛坯裂纹止裂中的应用[J]. 机械工程学报, 2013, 49(7):21-28. ZHANG H C, YU J, HAO S Z, et al. Application of electro-magnetic heat effect on arresting the crack in remanufacturing blank[J]. Journal of Mechanical Engineering, 2013, 49(7):21-28(in Chinese).
[17] 邓德伟, 刘倩倩, 牛婷婷, 等. 脉冲电流对奥氏体不锈钢止裂效果的影响[J]. 热加工工艺, 2015(16):49-52. DENG D W, LIU Q Q, NIU T T, et al. Effect of pulse current on crack arrest of austenitic stainless steel[J]. Hot Working Technology, 2015(16):49-52(in Chinese).
[18] HOSOI A, NAGAHAMA T, JU Y. Fatigue crack healing by a controlled high density electric current field[J]. Materials Science and Engineering:A, 2012, 533(1):38-42.
[19] HOSOI A, KISHI T, JU Y. Healing of fatigue crack by high-density electro pulsing in austenitic stainless steel treated with the surface-activated pre-coating[J]. Materials Science and Engineering:A, 2013, 6(9):4213-4225.
[20] 李超, 张凯锋, 蒋少松. 轻合金板材超塑成形中的脉冲电流加热方法及其宏微观分析[J]. 机械工程学报, 2011, 47(18):43-49. LI C, ZHANG K F, JIANG S S. Pulse current heating method for light alloy superplastic forming and macroscopic and microscopic effects analysis[J]. Journal of Mechanical Engineering, 2011, 47(18):43-49(in Chinese).
/
| 〈 |
|
〉 |
CJA