Calculation formula and test method of calendar life of metallic coating
Received date: 2015-09-30
Revised date: 2015-12-14
Online published: 2015-12-22
Through research on the test of coating corrosion damage, this paper finds out that the temperature-time(T-H) curve of coating corrosion and the T-H curve of metallic corrosion are consistent, and they have the same service environment spectrum. Since the calculation formula of metallic calendar life is deduced from the distribution regularities and service environment spectrum of T-H curve, the calculation formula of coating's calendar life is the same as that of the metallic calendar life. It is also revealed that metallic coating is sensitive to test temperature with some regularities. Hence, an effective test method to have the calendar life of coating is to increase the temperature of the test. To verify the above-mentioned conclusion, a comparative study of theoretical calculation and test of the calendar life of aluminum coating is also conducted.
ZHANG Fuze . Calculation formula and test method of calendar life of metallic coating[J]. ACTA AERONAUTICAET ASTRONAUTICA SINICA, 2016 , 37(2) : 390 -396 . DOI: 10.7527/S1000-6893.2015.0339
[1] 张福泽. 金属机件腐蚀损伤日历寿命计算模型和确定方法[J]. 航空学报, 1999, 20(1):75-79. ZHANG F Z. Calculation model and determination method of corrosion damage calendar life of metal parts[J]. Acta Aeronautica et Astronautica Sinica, 1999, 20(1):75-79(in Chinese).
[2] 张福泽. 飞机停放日历寿命腐蚀温度谱编制方法和相应腐蚀介质的确定[J]. 航空学报, 2001, 22(4):359-361. ZHANG F Z. Method for drawing up corrosion temperature spectrum of aircraft calendar life and determination of respective corrosion medium[J]. Acta Aeronautica et Astronautica Sinica, 2001, 22(4):359-361(in Chinese).
[3] 张福泽, 陈勃. Ly12cz和30CrMnSiA航空材料涂层失效的T-H曲线测试报告[R]. 北京:北京航空材料研究院, 2006. ZHANG F Z, CHEN B. T-H curves testing report of lose efficacy coating for Ly12cz and 30CrMnSiA aeronautical materials[R]. Beijing:Beijing Academy of Aeronautical Materials, 2006(in Chinese).
[4] ROKHLIN S I, KIMA J Y, NAGYA H, et al. Effect of pitting corrosion on fatigue crack initiation and fatigue life[J]. Engineering Fracture Mechanica, 1999, 62(4-5):425-444.
[5] 宋钧, 郭宏全. 三种航空材料腐蚀T-H曲线测试报告[R]. 北京:北京航空材料研究院, 2000. SONG J, GUO H Q. Testing report of corrosion T-H corves three testing report of kinds of aeronautical materials[R]. Beijng:Beijing Academy of Aeronautical Materials, 2000(in Chinese).
[6] LATANISION R M. Corrosion science, corrosion engineering, and advanced technologies[J]. Corrosion Science, 1995, 51(4):270-283.
[7] HEUSLER K E. Fundamental aspects of the corrosion of alloys[J]. Corrosion Science, 1997, 39(7):1177-1191.
[8] 张福泽, 叶序彬. 在25℃和-40℃环境下的3种航空材料的疲劳品质研究[J]. 航空学报, 2006, 27(3):1127-1129. ZHANG F Z, YE X B. Study on fatigue behavior of three kinds of aeronautical materials at 25℃ and-40℃[J]. Acta Aeronautica et Astronautica Sinica, 2006, 27(3):1127-1129(in Chinese).
[9] 张福泽, 叶序彬. 在25℃和-40℃环境下的3种航空材料的裂纹扩展品质研究[J]. 航空学报, 2007, 28(3):593-595. ZHANG F Z, YE X B. Study on crack growth behaviors of three kinds of aeronautical materials at 25℃ and-40℃[J]. Acta Aeronautica et Astronautica Sinica, 2007, 28(3):593-595(in Chinese).
/
| 〈 |
|
〉 |
CJA