Microstructure and Friction Wear Properties of Twin-roll Casting Magnesium Alloy AZ41
Received date: 2013-07-18
Revised date: 2013-08-15
Online published: 2013-08-25
Supported by
National Natural Science Foundation of China (U1134101); Natural Science Foundation of Shandong Province (ZR2011EMM003)
In order to analyze the friction wear properties of casting magnesium alloy AZ41 sheet, a twin-roll casting method is used for preparing a magnesium alloy AZ41 sheet, and the microstructure of the AZ41 sheet under the condition of twin-roll casting and heat-treatment are observed respectively. The effects of sliding speeds and loads on its friction wear properties are studied by a dry sliding friction test, and the worn surface morphologies are observed by an SEM in order to reveal its wear mechanism. Finally, the stress distribution during the friction wear processes is simulated by finite element analysis method. The results show that there is a large quantity of compression twin crystals in (1012) of the prepared materials and these crystals turn into equiaxed grains after heat-treatment; friction coefficient of the material gradually increases with the increase of the speed, and within a certain range of the load, the friction coefficient is reduced with the increase of the load. Wear weight loss increases with increasing load and speed, and the wear mechanism of the material is abrasive wear in low loads, which is accompanied by oxidation wear, but with high loads the main mechanism is adhesive wear.
Key words： twin-roll casting; magnesium alloys; microstructure; friction wear; wear mechanism
SONG Linghui , WANG Shouren , CHO Jae-hyung . Microstructure and Friction Wear Properties of Twin-roll Casting Magnesium Alloy AZ41[J]. ACTA AERONAUTICAET ASTRONAUTICA SINICA, 2014 , 35(6) : 1733 -1739 . DOI: 10.7527/S1000-6893.2013.0367
[1] Song S X,Horton J A, Kim N J, et al. Deformation behavior of a twin-roll-cast Mg-6Zn-0.5Mn-0.3Cu-0.02Zr alloy at intermediate temperatures[J]. Scripta Materialia, 2007, 56(5): 393-395.
[2] Wang S C, Chou C P, Fann Y C. Microstructures and mechanical properties of modified AZ31-Zr-Sc alloys[J]. Materials Science and Engineering A, 2008, 485(1-2):428-438.
[3] Kim W J, Lee J B, Kim W Y, et al. Microstructure and mechanical properties of Mg-Al-Zn alloy sheets severely deformed by asymmetrical rolling[J]. Scripta Materialia, 2007, 56(4): 309-312.
[4] Liu G J, Xu J, Yang L Q. Research and technology development on sheet casting of magnesium alloys[J]. Chinese Journal of Rare Metals, 2012, 36(3): 477-482.(in Chinese) 刘国钧, 徐骏, 杨柳青. 镁合金板带铸轧技术与进展[J].稀有金属, 2012, 36(3): 477-482.
[5] Weng W P, Yan Y Q, Chen Q, et al. Microstructure of twin-roll casting magnesium alloy strip[J]. Special Casting & Nonferrous Alloys, 2007, 27(11): 827-828. (in Chinese) 翁文凭, 闫蕴琪, 陈琦, 等. 双辊铸轧镁合金板坯微观组织特征[J]. 特种铸造及有色合金, 2007, 27(11): 827-828.
[6] Watari H, Davey K, Rasgado M T, et al. Semi-solid manufacturing process of magnesium alloys by twin-roll casting[J]. Journal of Materials Processing Technology, 2004, 155-156: 1662-1667.
[7] Anbuselvan S, Ramanathan S. Dry sliding wear behavior of as-cast ZE41A magnesium alloy[J]. Materials and Design, 2010, 31(4): 1930-1936.
[8] Fouad Y, El Batanouny M. Effect of surface treatment on wear behavior of magnesium alloy AZ31[J]. Alexandria Engineering Journal, 2011, 50(1): 19-22.
[9] Wang S Q, Yang Z R, Zhao Y T, et al. Sliding wear characteristics of AZ91D alloy at ambient temperatures of 25-200℃[J]. Tribology Letters, 2010, 39(1): 39-45.
[10] Habibnejad-koraygem M, Mahmudi R, Ghasemi H M, et al. Tribological behavior of pure Mg and AZ31 magnesium alloy strengthened by Al2O3 nano-particles[J]. Wear, 2010, 268(3-4): 405-412.
[11] Hiratsuka K, Enomoto A, Sasada T. Friction and wear of Al2O3, ZrO2 and SiO2 rubbed against pure metals[J]. Wear, 1992, 153(2): 361-373
[12] Li D N, Xiao X Q, Wang L M, et al. Study on friction and wear characteristics of die casting magnesium alloy AZ91D[J]. China Mechanical Engineering, 2006, 17(19): 2072-2079. (in Chinese) 李东南, 肖雪清, 王黎明, 等. 压铸镁合金AZ91D 摩擦磨损性能的研究[J]. 中国机械工程, 2006, 17(19): 2072-2079.
[13] Chen H, Alpas A T. Sliding wear map for the magnesium alloy Mg-9Al-0.9Zn (AZ91)[J]. Wear, 2000, 246(1-2): 106-116.
[14] An J, Li R G, Lu Y, et al. Dry sliding wear behavior of magnesium alloy[J]. Wear, 2008, 265(1-2): 97-104.
[15] Liu Y, Yang G N,Zhang Z D, et al. Dry sliding friction and wear properties of AZ91 Mg alloy[J]. Journal of Jinan University: Natural Science, 2010, 31(5): 490-494. (in Chinese) 刘英, 杨冠男, 张兆东, 等. AZ91镁合金的干滑动摩擦磨损性能研究[J]. 暨南大学学报: 自然科学版, 2010, 31(5): 490-494.
[16] Taltavull C, Torres B, López A J, et al. Dry sliding wear behavior of AM60B magnesium alloy[J]. Wear, 2013, 301(1-2): 615-625.
/
| 〈 |
|
〉 |
CJA