复合材料层合板结构冲击损伤数值模拟的损伤力学模型
收稿日期: 2015-10-19
修回日期: 2015-11-16
网络出版日期: 2016-01-15
基金资助
国家自然科学基金(11202098)
Damage mechanics model for simulating impact responses of composite laminated structures
Received date: 2015-10-19
Revised date: 2015-11-16
Online published: 2016-01-15
Supported by
National Natural Science Foundation of China (11202098)
针对复合材料结构低速冲击损伤问题,基于连续损伤力学提出了一种动力学冲击条件下的三维损伤数值模型。模型中区分了层内损伤(纤维拉伸与压缩失效、纤维间拉伸与压缩失效)和层间分层损伤不同的失效模式。采用三维Puck失效准则与考虑压缩抑制效应的Aymerich准则对上述两类损伤进行判定,材料失效后基于连续损伤力学中线性软化模型对材料损伤进行演化。模型中考虑了复合材料层合板结构中子层的就位效应和损伤分析中的“连锁效应”。通过对Shi的冲击试验进行数值模拟,模型预测的冲击接触载荷、分层形状和尺寸与试验结果吻合较好,证明了所提出的数值模型对复合材料层合板结构低速冲击损伤预测的有效性。
刘向民 , 姚卫星 , 陈方 . 复合材料层合板结构冲击损伤数值模拟的损伤力学模型[J]. 航空学报, 2016 , 37(10) : 3054 -3063 . DOI: 10.7527/S1000-6893.2015.0345
Based on continuum damage mechanics, a three-dimensional damage mechanics model was proposed to simulate low-velocity impact responses of composite laminated structures under the condition of dynamic. This model is capable to predict several possible in-plane failure modes (e.g., fibre tensile failure, fiber compressive failure, inter fiber tensile failure and inter fiber compressive failure) and interlaminar failure modes. Three-dimensional Puck failure criterion was used to conduct in-plane failure determination, and Aymerich failure criterion was used to conduct delamination failure determination. After damage initiation, linear-softening model was used to describe material properties' evolution process. In addition, the lamina's in-situ effect and structures' chain destruction were also taken into consideration. By using this model, a numerical example was finished. The final result shows that the predicted impact load, delamination shape and size have a relatively good agreement with Shi's experimental data. Therefore, the rationality and effectiveness of the developed numerical model for predicting low-velocity impact responses of composite laminated structures are shown.
[1] 杨光松. 损伤力学与复合材料损伤[M]. 北京:国防工业出版社, 1995:117-120. YANG G S. Damage mechanics and composite material damage[M]. Beijing:National Defence Industry Press, 1995:117-120(in Chinese).
[2] SWANSON S R. Limits of quasi-static solutions in impact of composite structures[J]. Composites Engineering, 1992, 2(4):261-267.
[3] SUN C T, JIH C J. A quasi-static treatment of delamination crack propagation in laminates subjected to low velocity impact[M]. Basel:Technomic Publishing AG, 1992:949.
[4] DE MOUTA M, MARQUES A T. Prediction of low velocity impact damage in carbon-epoxy laminates[J]. Composites Part A:Applied Science and Manufacturing, 2002, 33(3):361-368.
[5] WISHEART M, RICHARDSON M. The finite element analysis of impact induced delamination in composite materials using a novel interface element[J]. Composites Part A:Applied Science and Manufacturing, 1998, 29(3):301-313.
[6] 张海波. 新3D界面元在复合材料层合板分层损伤数值模拟中的应用[D]. 天津:天津大学, 2009:32-54. ZHANG H B. A new 3D interface element for delamination simulation of laminated plates[D]. Tianjin:Tianjin University, 2009:32-54(in Chinese).
[7] 彭文杰, 陈建桥, 魏俊红, 等. 考虑逐步失效的层合板低速冲击损伤研究[J]. 华中科技大学学报(自然科学版), 2010, 38(4):129-132. PENG W J, CHEN J Q, WEI J H, et al. Numerical simulation of delamination in laminates with sequential failure low-velocity impact considering[J]. Journal of Huazhong University of Science and Technology (Natural Science Edition), 2010, 38(4):129-132(in Chinese).
[8] CHOI H Y, CHANG F. A model for predicting damage in graphite/epoxy laminated composites resulting from low-velocity point impact[J]. Journal of Composite Materials, 1992, 26(14):2134-2169.
[9] HOU J P, PETRINIC N, RUIZ C, et al. Prediction of impact damage in composite plates[J]. Composites Science and Technology, 2000, 60(2):273-281.
[10] 徐颖. 复合材料层合板冲击损伤及冲击后疲劳寿命研究[D]. 南京:南京航空航天大学, 2007:30-37. XU Y.Research on impact damage of laminates and fatigue life of impacted laminates[D]. Nanjing:Nanjing University of Aeronautics & Astronautics, 2007:30-37(in Chinese).
[11] AYMERICH F, DORE F, PRIOLO P. Prediction of impact-induced delamination in cross-ply composite laminates using cohesive interface elements[J]. Composites Science and Technology, 2008, 68(12):2383-2390.
[12] SHI Y, SWAIT T, SOUTIS C. Modelling damage evolution in composite laminates subjected to low velocity impact[J]. Composite Structures, 2012, 94(9):2902-2913.
[13] 朱炜垚, 许希武. 复合材料层合板低速冲击损伤的有限元模拟[J]. 复合材料学报, 2010, 27(6):200-207. ZHU W Y, XU X W. Finite element simulation of low velocity impact damage on composite laminates[J]. Acta Materiae Compositae Sinica, 2010, 27(6):200-207(in Chinese).
[14] 陈普会, 李念. 复合材料层合板低速冲击损伤的预测模型[J]. 南京航空航天大学学报, 2014, 46(3):341-348. CHEN P H, LI N.Damage prediction model for composite laminates subjected to low velocity impact[J]. Journal of Nanjing University of Aeronautics & Astronautics, 2014, 46(3):341-348(in Chinese).
[15] SINGH H, NAMALA K K, MAHAJAN P. A damage evolution study of E-glass/epoxy composite under low velocity impact[J]. Composites Part B:Engineering, 2015, 76:235-248.
[16] 孟达, 王家臣, 王进学. 房柱式开采上覆岩层破坏与垮落机理[J]. 煤炭学报, 2007, 32(6):577-580. MENG D, WANG J C, WANG J X.Mechanism on the failure and caving of roof strata in pillar and house mining[J]. Journal of China Coal Society, 2007, 32(6):577-580(in Chinese).
[17] PUCK A. Failure analysis of FRP laminates by means of physically based phenomenological models[J]. Composites Science and Technology, 1998, 58(7):1045-1067.
[18] PUCK A, KOPP J, KNOPS M. Guidelines for the determination of the parameters in Puck's action plane strength criterion[J]. Composites Science and Technology, 2002, 62(3):371-378.
[19] CHANG K, LIU S, CHANG F. Damage tolerance of laminated composites containing an open hole and subjected to tensile loadings[J]. Journal of Composite Materials, 1991, 25(3):274-301.
[20] KNOPS M. Analysis of failure in fiber polymer laminates:The theory of Alfred Puck[M]. Berlin, Heidelberg:Springer, 2008:65-79.
[21] CAMANHO P P, MATTHEWS F L. A progressive damage model for mechanically fastened joints in composite laminates[J]. Journal of Composite Materials, 1999, 33(24):2248-2280.
[22] 吴义韬, 姚卫星, 吴富强. 复合材料层合板面内渐进损伤分析的CDM模型[J]. 力学学报, 2014, 46(1):94-104. WU Y T, YAO W X, WU F Q. CDM model for intralaminar progressive damage analysis of composite laminates[J]. Chinese Journal of Theoretical and Applied Mechanics, 2014, 46(1):94-104(in Chinese).
[23] 李念, 陈普会. 复合材料层合板低速冲击损伤分析的连续介质损伤力学模型[J]. 力学学报, 2015, 43(3):458-470. LI N, CHEN P H. Continuum damage mechanics model for low-velocity impact damage analysis of composite laminates[J]. Chinese Journal of Theoretical and Applied Mechanics, 2015, 43(3):458-470(in Chinese).
[24] BENZEGGAGH M L, KENANE M. Measurement of mixed-mode delamination fracture toughness of unidi-rectional glass/epoxy composites with mixed-mode bending apparatus[J]. Composites Science and Technology, 1996, 56(4):439-449.
[25] 江大志, 王兴业, 沈为, 等. 波速测量层合复合材料冲击损伤实验[J]. 国防科技大学学报, 1997, 19(1):27-30. JIANG D Z, WANG X Y, SHEN W, et al. Impact damage of composite laminates measured by variance of wave speed[J]. Journal of National University of Defense Technology, 1997, 19(1):27-30(in Chinese).
/
〈 | 〉 |